5010-F Aluminum
5010-F aluminum is 5010 aluminum in the as-fabricated (no temper or treatment) condition. It has the lowest strength compared to the other variants of 5010 aluminum. The graph bars on the material properties cards below compare 5010-F aluminum to: 5000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
69 GPa 10 x 106 psi
Elongation at Break
23 %
Fatigue Strength
35 MPa 5.0 x 103 psi
Poisson's Ratio
0.33
Shear Modulus
26 GPa 3.8 x 106 psi
Shear Strength
64 MPa 9.3 x 103 psi
Tensile Strength: Ultimate (UTS)
100 MPa 15 x 103 psi
Tensile Strength: Yield (Proof)
38 MPa 5.5 x 103 psi
Thermal Properties
Latent Heat of Fusion
400 J/g
Maximum Temperature: Mechanical
180 °C 360 °F
Melting Completion (Liquidus)
650 °C 1190 °F
Melting Onset (Solidus)
630 °C 1160 °F
Specific Heat Capacity
900 J/kg-K 0.21 BTU/lb-°F
Thermal Conductivity
200 W/m-K 120 BTU/h-ft-°F
Thermal Expansion
23 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
45 % IACS
Electrical Conductivity: Equal Weight (Specific)
150 % IACS
Otherwise Unclassified Properties
Base Metal Price
9.5 % relative
Density
2.7 g/cm3 170 lb/ft3
Embodied Carbon
8.2 kg CO2/kg material
Embodied Energy
150 MJ/kg 66 x 103 BTU/lb
Embodied Water
1190 L/kg 140 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
19 MJ/m3
Resilience: Unit (Modulus of Resilience)
10 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
50 points
Strength to Weight: Axial
10 points
Strength to Weight: Bending
18 points
Thermal Diffusivity
82 mm2/s
Thermal Shock Resistance
4.5 points
Alloy Composition
| Al | 97.1 to 99.7 | |
| Mg | 0.2 to 0.6 | |
| Fe | 0 to 0.7 | |
| Mn | 0.1 to 0.3 | |
| Si | 0 to 0.4 | |
| Zn | 0 to 0.3 | |
| Cu | 0 to 0.25 | |
| Cr | 0 to 0.15 | |
| Ti | 0 to 0.1 | |
| res. | 0 to 0.15 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
Aluminum: Properties and Physical Metallurgy, John E. Hatch (editor), 1984
ASTM B209: Standard Specification for Aluminum and Aluminum-Alloy Sheet and Plate
EN 485-2: Aluminium and aluminium alloys. Sheet, strip and plate. Mechanical properties
EN 573-3: Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products
Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993