5026-H34 Aluminum
5026-H34 aluminum is 5026 aluminum in the H34 temper. To achieve this temper, the metal is strain hardened, and then stabilized, to a strength that is roughly halfway between annealed (O) and full-hard (H38).
The graph bars on the material properties cards below compare 5026-H34 aluminum to: 5000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
70 GPa 10 x 106 psi
Elongation at Break
11 %
Fatigue Strength
140 MPa 20 x 103 psi
Poisson's Ratio
0.33
Shear Modulus
26 GPa 3.8 x 106 psi
Shear Strength
160 MPa 24 x 103 psi
Tensile Strength: Ultimate (UTS)
270 MPa 39 x 103 psi
Tensile Strength: Yield (Proof)
230 MPa 33 x 103 psi
Thermal Properties
Latent Heat of Fusion
400 J/g
Maximum Temperature: Mechanical
210 °C 420 °F
Melting Completion (Liquidus)
650 °C 1200 °F
Melting Onset (Solidus)
510 °C 960 °F
Specific Heat Capacity
890 J/kg-K 0.21 BTU/lb-°F
Thermal Conductivity
130 W/m-K 75 BTU/h-ft-°F
Thermal Expansion
23 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
31 % IACS
Electrical Conductivity: Equal Weight (Specific)
99 % IACS
Otherwise Unclassified Properties
Base Metal Price
9.5 % relative
Density
2.8 g/cm3 170 lb/ft3
Embodied Carbon
8.9 kg CO2/kg material
Embodied Energy
150 MJ/kg 66 x 103 BTU/lb
Embodied Water
1150 L/kg 140 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
29 MJ/m3
Resilience: Unit (Modulus of Resilience)
360 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
49 points
Strength to Weight: Axial
27 points
Strength to Weight: Bending
34 points
Thermal Diffusivity
52 mm2/s
Thermal Shock Resistance
12 points
Alloy Composition
| Al | 88.2 to 94.7 | |
| Mg | 3.9 to 4.9 | |
| Mn | 0.6 to 1.8 | |
| Si | 0.55 to 1.4 | |
| Fe | 0.2 to 1.0 | |
| Zn | 0 to 1.0 | |
| Cu | 0.1 to 0.8 | |
| Cr | 0 to 0.3 | |
| Zr | 0 to 0.3 | |
| Ti | 0 to 0.2 | |
| res. | 0 to 0.15 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
Iron in Aluminium Alloys: Impurity and Alloying Element, N. A. Belov et al., 2002
Handbook of Aluminum vol. 2: Alloy Production and Materials Manufacturing, George Totten and D. Scott MacKenzie (editors), 2003
EN 485-2: Aluminium and aluminium alloys. Sheet, strip and plate. Mechanical properties
ISO 6361-2: Wrought aluminium and aluminium alloys - Sheets, strips and plates - Part 2: Mechanical properties
EN 573-3: Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products