5049-H112 Aluminum
5049-H112 aluminum is 5049 aluminum in the H112 temper. This temper is actually just a variation on F (as-fabricated) that allows for the possibility of very limited strain hardening or heat treatment, under certain conditions.
The graph bars on the material properties cards below compare 5049-H112 aluminum to: 5000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
62
Elastic (Young's, Tensile) Modulus
69 GPa 10 x 106 psi
Elongation at Break
14 %
Fatigue Strength
84 MPa 12 x 103 psi
Poisson's Ratio
0.33
Shear Modulus
26 GPa 3.8 x 106 psi
Shear Strength
130 MPa 19 x 103 psi
Tensile Strength: Ultimate (UTS)
220 MPa 32 x 103 psi
Tensile Strength: Yield (Proof)
97 MPa 14 x 103 psi
Thermal Properties
Latent Heat of Fusion
400 J/g
Maximum Temperature: Mechanical
190 °C 370 °F
Melting Completion (Liquidus)
650 °C 1200 °F
Melting Onset (Solidus)
620 °C 1140 °F
Specific Heat Capacity
900 J/kg-K 0.21 BTU/lb-°F
Thermal Conductivity
140 W/m-K 80 BTU/h-ft-°F
Thermal Expansion
24 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
35 % IACS
Electrical Conductivity: Equal Weight (Specific)
110 % IACS
Otherwise Unclassified Properties
Base Metal Price
9.5 % relative
Density
2.7 g/cm3 170 lb/ft3
Embodied Carbon
8.5 kg CO2/kg material
Embodied Energy
150 MJ/kg 66 x 103 BTU/lb
Embodied Water
1180 L/kg 140 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
25 MJ/m3
Resilience: Unit (Modulus of Resilience)
68 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
50 points
Strength to Weight: Axial
22 points
Strength to Weight: Bending
30 points
Thermal Diffusivity
56 mm2/s
Thermal Shock Resistance
9.7 points
Alloy Composition
| Al | 94.7 to 97.9 | |
| Mg | 1.6 to 2.5 | |
| Mn | 0.5 to 1.1 | |
| Fe | 0 to 0.5 | |
| Si | 0 to 0.4 | |
| Cr | 0 to 0.3 | |
| Zn | 0 to 0.2 | |
| Ti | 0 to 0.1 | |
| Cu | 0 to 0.1 | |
| res. | 0 to 0.15 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
EN 755-2: Aluminium and aluminium alloys. Extruded rod/bar, tube and profiles. Mechanical properties
EN 485-2: Aluminium and aluminium alloys. Sheet, strip and plate. Mechanical properties
ISO 6361-2: Wrought aluminium and aluminium alloys - Sheets, strips and plates - Part 2: Mechanical properties
EN 573-3: Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products
Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993