5049-H28 Aluminum
5049-H28 aluminum is 5049 aluminum in the H28 temper. This is the strongest temper normally produced through the action of strain hardening followed by partial annealing. It is closely related to H18. It has the highest strength compared to the other variants of 5049 aluminum.
The graph bars on the material properties cards below compare 5049-H28 aluminum to: 5000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
87
Elastic (Young's, Tensile) Modulus
69 GPa 10 x 106 psi
Elongation at Break
4.0 %
Fatigue Strength
110 MPa 16 x 103 psi
Poisson's Ratio
0.33
Shear Modulus
26 GPa 3.8 x 106 psi
Shear Strength
190 MPa 28 x 103 psi
Tensile Strength: Ultimate (UTS)
330 MPa 48 x 103 psi
Tensile Strength: Yield (Proof)
260 MPa 37 x 103 psi
Thermal Properties
Latent Heat of Fusion
400 J/g
Maximum Temperature: Mechanical
190 °C 370 °F
Melting Completion (Liquidus)
650 °C 1200 °F
Melting Onset (Solidus)
620 °C 1140 °F
Specific Heat Capacity
900 J/kg-K 0.21 BTU/lb-°F
Thermal Conductivity
140 W/m-K 80 BTU/h-ft-°F
Thermal Expansion
24 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
35 % IACS
Electrical Conductivity: Equal Weight (Specific)
110 % IACS
Otherwise Unclassified Properties
Base Metal Price
9.5 % relative
Density
2.7 g/cm3 170 lb/ft3
Embodied Carbon
8.5 kg CO2/kg material
Embodied Energy
150 MJ/kg 66 x 103 BTU/lb
Embodied Water
1180 L/kg 140 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
12 MJ/m3
Resilience: Unit (Modulus of Resilience)
480 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
50 points
Strength to Weight: Axial
34 points
Strength to Weight: Bending
39 points
Thermal Diffusivity
56 mm2/s
Thermal Shock Resistance
15 points
Alloy Composition
| Al | 94.7 to 97.9 | |
| Mg | 1.6 to 2.5 | |
| Mn | 0.5 to 1.1 | |
| Fe | 0 to 0.5 | |
| Si | 0 to 0.4 | |
| Cr | 0 to 0.3 | |
| Zn | 0 to 0.2 | |
| Ti | 0 to 0.1 | |
| Cu | 0 to 0.1 | |
| res. | 0 to 0.15 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
EN 755-2: Aluminium and aluminium alloys. Extruded rod/bar, tube and profiles. Mechanical properties
EN 485-2: Aluminium and aluminium alloys. Sheet, strip and plate. Mechanical properties
ISO 6361-2: Wrought aluminium and aluminium alloys - Sheets, strips and plates - Part 2: Mechanical properties
EN 573-3: Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products
Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993