5050-H111 Aluminum
5050-H111 aluminum is 5050 aluminum in the H111 temper. To achieve this temper, the metal is strain hardened to a strength that is lower than what is permissible for H11 (1/8-hard). It has the second lowest strength and second highest ductility compared to the other variants of 5050 aluminum.
The graph bars on the material properties cards below compare 5050-H111 aluminum to: 5000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
36
Elastic (Young's, Tensile) Modulus
68 GPa 9.9 x 106 psi
Elongation at Break
21 %
Fatigue Strength
45 MPa 6.5 x 103 psi
Poisson's Ratio
0.33
Shear Modulus
26 GPa 3.7 x 106 psi
Shear Strength
91 MPa 13 x 103 psi
Tensile Strength: Ultimate (UTS)
150 MPa 21 x 103 psi
Tensile Strength: Yield (Proof)
50 MPa 7.3 x 103 psi
Thermal Properties
Latent Heat of Fusion
400 J/g
Maximum Temperature: Mechanical
180 °C 360 °F
Melting Completion (Liquidus)
650 °C 1200 °F
Melting Onset (Solidus)
630 °C 1160 °F
Specific Heat Capacity
900 J/kg-K 0.22 BTU/lb-°F
Thermal Conductivity
190 W/m-K 110 BTU/h-ft-°F
Thermal Expansion
24 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
50 % IACS
Electrical Conductivity: Equal Weight (Specific)
170 % IACS
Otherwise Unclassified Properties
Base Metal Price
9.5 % relative
Calomel Potential
-760 mV
Density
2.7 g/cm3 170 lb/ft3
Embodied Carbon
8.4 kg CO2/kg material
Embodied Energy
150 MJ/kg 66 x 103 BTU/lb
Embodied Water
1190 L/kg 140 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
23 MJ/m3
Resilience: Unit (Modulus of Resilience)
19 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
50 points
Strength to Weight: Axial
15 points
Strength to Weight: Bending
23 points
Thermal Diffusivity
79 mm2/s
Thermal Shock Resistance
6.4 points
Alloy Composition
| Al | 96.3 to 98.9 | |
| Mg | 1.1 to 1.8 | |
| Fe | 0 to 0.7 | |
| Si | 0 to 0.4 | |
| Zn | 0 to 0.25 | |
| Cu | 0 to 0.2 | |
| Mn | 0 to 0.1 | |
| Cr | 0 to 0.1 | |
| res. | 0 to 0.15 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM B547: Standard Specification for Aluminum and Aluminum-Alloy Formed and Arc-Welded Round Tube
ASTM B209: Standard Specification for Aluminum and Aluminum-Alloy Sheet and Plate
EN 485-2: Aluminium and aluminium alloys. Sheet, strip and plate. Mechanical properties
Aluminum Standards and Data, Aluminum Association Inc., 2013
ISO 6361-2: Wrought aluminium and aluminium alloys - Sheets, strips and plates - Part 2: Mechanical properties
EN 573-3: Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products