5050-H28 Aluminum
5050-H28 aluminum is 5050 aluminum in the H28 temper. This is the strongest temper normally produced through the action of strain hardening followed by partial annealing. It is closely related to H18. The graph bars on the material properties cards below compare 5050-H28 aluminum to: 5000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
67
Elastic (Young's, Tensile) Modulus
68 GPa 9.9 x 106 psi
Elongation at Break
2.2 %
Fatigue Strength
83 MPa 12 x 103 psi
Poisson's Ratio
0.33
Shear Modulus
26 GPa 3.7 x 106 psi
Shear Strength
140 MPa 20 x 103 psi
Tensile Strength: Ultimate (UTS)
250 MPa 36 x 103 psi
Tensile Strength: Yield (Proof)
210 MPa 30 x 103 psi
Thermal Properties
Latent Heat of Fusion
400 J/g
Maximum Temperature: Mechanical
180 °C 360 °F
Melting Completion (Liquidus)
650 °C 1200 °F
Melting Onset (Solidus)
630 °C 1160 °F
Specific Heat Capacity
900 J/kg-K 0.22 BTU/lb-°F
Thermal Conductivity
190 W/m-K 110 BTU/h-ft-°F
Thermal Expansion
24 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
50 % IACS
Electrical Conductivity: Equal Weight (Specific)
170 % IACS
Otherwise Unclassified Properties
Base Metal Price
9.5 % relative
Calomel Potential
-760 mV
Density
2.7 g/cm3 170 lb/ft3
Embodied Carbon
8.4 kg CO2/kg material
Embodied Energy
150 MJ/kg 66 x 103 BTU/lb
Embodied Water
1190 L/kg 140 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
5.2 MJ/m3
Resilience: Unit (Modulus of Resilience)
310 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
50 points
Strength to Weight: Axial
25 points
Strength to Weight: Bending
32 points
Thermal Diffusivity
79 mm2/s
Thermal Shock Resistance
11 points
Alloy Composition
| Al | 96.3 to 98.9 | |
| Mg | 1.1 to 1.8 | |
| Fe | 0 to 0.7 | |
| Si | 0 to 0.4 | |
| Zn | 0 to 0.25 | |
| Cu | 0 to 0.2 | |
| Mn | 0 to 0.1 | |
| Cr | 0 to 0.1 | |
| res. | 0 to 0.15 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM B547: Standard Specification for Aluminum and Aluminum-Alloy Formed and Arc-Welded Round Tube
ASTM B209: Standard Specification for Aluminum and Aluminum-Alloy Sheet and Plate
EN 485-2: Aluminium and aluminium alloys. Sheet, strip and plate. Mechanical properties
Aluminum Standards and Data, Aluminum Association Inc., 2013
ISO 6361-2: Wrought aluminium and aluminium alloys - Sheets, strips and plates - Part 2: Mechanical properties
EN 573-3: Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products