5454-F Aluminum
5454-F aluminum is 5454 aluminum in the as-fabricated (no temper or treatment) condition. It has the lowest strength and highest ductility compared to the other variants of 5454 aluminum. The graph bars on the material properties cards below compare 5454-F aluminum to: 5000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
69 GPa 10 x 106 psi
Elongation at Break
18 %
Fatigue Strength
83 MPa 12 x 103 psi
Poisson's Ratio
0.33
Shear Modulus
26 GPa 3.8 x 106 psi
Shear Strength
140 MPa 20 x 103 psi
Tensile Strength: Ultimate (UTS)
230 MPa 33 x 103 psi
Tensile Strength: Yield (Proof)
97 MPa 14 x 103 psi
Thermal Properties
Latent Heat of Fusion
400 J/g
Maximum Temperature: Mechanical
190 °C 370 °F
Melting Completion (Liquidus)
650 °C 1190 °F
Melting Onset (Solidus)
600 °C 1110 °F
Specific Heat Capacity
900 J/kg-K 0.22 BTU/lb-°F
Thermal Conductivity
130 W/m-K 78 BTU/h-ft-°F
Thermal Expansion
24 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
34 % IACS
Electrical Conductivity: Equal Weight (Specific)
110 % IACS
Otherwise Unclassified Properties
Base Metal Price
9.5 % relative
Density
2.7 g/cm3 170 lb/ft3
Embodied Carbon
8.6 kg CO2/kg material
Embodied Energy
150 MJ/kg 66 x 103 BTU/lb
Embodied Water
1180 L/kg 140 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
33 MJ/m3
Resilience: Unit (Modulus of Resilience)
68 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
50 points
Strength to Weight: Axial
23 points
Strength to Weight: Bending
30 points
Thermal Diffusivity
55 mm2/s
Thermal Shock Resistance
10 points
Alloy Composition
| Al | 94.5 to 97.1 | |
| Mg | 2.4 to 3.0 | |
| Mn | 0.5 to 1.0 | |
| Fe | 0 to 0.4 | |
| Si | 0 to 0.25 | |
| Cr | 0.050 to 0.2 | |
| Zn | 0 to 0.25 | |
| Ti | 0 to 0.2 | |
| Cu | 0 to 0.1 | |
| res. | 0 to 0.15 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM B547: Standard Specification for Aluminum and Aluminum-Alloy Formed and Arc-Welded Round Tube
Advanced Materials in Automotive Engineering, Jason Rowe (editor), 2012
ASTM B209: Standard Specification for Aluminum and Aluminum-Alloy Sheet and Plate
EN 755-2: Aluminium and aluminium alloys. Extruded rod/bar, tube and profiles. Mechanical properties
EN 485-2: Aluminium and aluminium alloys. Sheet, strip and plate. Mechanical properties
Aluminum Standards and Data, Aluminum Association Inc., 2013
EN 573-3: Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products
Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993