5652-H32 Aluminum
5652-H32 aluminum is 5652 aluminum in the H32 temper. To achieve this temper, the metal is strain hardened, and then stabilized, to a strength that is roughly a quarter of the way between annealed (O) and full-hard (H38).
It has the second highest ductility compared to the other variants of 5652 aluminum.
The graph bars on the material properties cards below compare 5652-H32 aluminum to: 5000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
60
Elastic (Young's, Tensile) Modulus
68 GPa 9.9 x 106 psi
Elongation at Break
13 %
Fatigue Strength
120 MPa 17 x 103 psi
Poisson's Ratio
0.33
Shear Modulus
26 GPa 3.7 x 106 psi
Shear Strength
140 MPa 20 x 103 psi
Tensile Strength: Ultimate (UTS)
230 MPa 34 x 103 psi
Tensile Strength: Yield (Proof)
190 MPa 28 x 103 psi
Thermal Properties
Latent Heat of Fusion
400 J/g
Maximum Temperature: Mechanical
190 °C 370 °F
Melting Completion (Liquidus)
650 °C 1200 °F
Melting Onset (Solidus)
610 °C 1120 °F
Specific Heat Capacity
900 J/kg-K 0.22 BTU/lb-°F
Thermal Conductivity
140 W/m-K 80 BTU/h-ft-°F
Thermal Expansion
24 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
35 % IACS
Electrical Conductivity: Equal Weight (Specific)
120 % IACS
Otherwise Unclassified Properties
Base Metal Price
9.5 % relative
Density
2.7 g/cm3 170 lb/ft3
Embodied Carbon
8.6 kg CO2/kg material
Embodied Energy
150 MJ/kg 66 x 103 BTU/lb
Embodied Water
1190 L/kg 140 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
29 MJ/m3
Resilience: Unit (Modulus of Resilience)
260 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
51 points
Strength to Weight: Axial
24 points
Strength to Weight: Bending
31 points
Thermal Diffusivity
57 mm2/s
Thermal Shock Resistance
10 points
Alloy Composition
| Al | 95.8 to 97.7 | |
| Mg | 2.2 to 2.8 | |
| Cr | 0.15 to 0.35 | |
| Si | 0 to 0.4 | |
| Fe | 0 to 0.4 | |
| Zn | 0 to 0.1 | |
| Cu | 0 to 0.040 | |
| Mn | 0 to 0.010 | |
| res. | 0 to 0.15 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM B209: Standard Specification for Aluminum and Aluminum-Alloy Sheet and Plate
Aluminum Standards and Data, Aluminum Association Inc., 2013
ASM Specialty Handbook: Aluminum and Aluminum Alloys, J. R. Davis (editor), 1993
CRC Materials Science and Engineering Handbook, 4th ed., James F. Shackelford et al. (editors), 2015