5652-O Aluminum
5652-O aluminum is 5652 aluminum in the annealed condition. It has the highest ductility compared to the other variants of 5652 aluminum. The graph bars on the material properties cards below compare 5652-O aluminum to: 5000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
47
Elastic (Young's, Tensile) Modulus
68 GPa 9.9 x 106 psi
Elongation at Break
25 %
Fatigue Strength
110 MPa 16 x 103 psi
Poisson's Ratio
0.33
Shear Modulus
26 GPa 3.7 x 106 psi
Shear Strength
130 MPa 18 x 103 psi
Tensile Strength: Ultimate (UTS)
190 MPa 28 x 103 psi
Tensile Strength: Yield (Proof)
84 MPa 12 x 103 psi
Thermal Properties
Latent Heat of Fusion
400 J/g
Maximum Temperature: Mechanical
190 °C 370 °F
Melting Completion (Liquidus)
650 °C 1200 °F
Melting Onset (Solidus)
610 °C 1120 °F
Specific Heat Capacity
900 J/kg-K 0.22 BTU/lb-°F
Thermal Conductivity
140 W/m-K 80 BTU/h-ft-°F
Thermal Expansion
24 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
35 % IACS
Electrical Conductivity: Equal Weight (Specific)
120 % IACS
Otherwise Unclassified Properties
Base Metal Price
9.5 % relative
Density
2.7 g/cm3 170 lb/ft3
Embodied Carbon
8.6 kg CO2/kg material
Embodied Energy
150 MJ/kg 66 x 103 BTU/lb
Embodied Water
1190 L/kg 140 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
39 MJ/m3
Resilience: Unit (Modulus of Resilience)
52 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
51 points
Strength to Weight: Axial
20 points
Strength to Weight: Bending
27 points
Thermal Diffusivity
57 mm2/s
Thermal Shock Resistance
8.4 points
Alloy Composition
| Al | 95.8 to 97.7 | |
| Mg | 2.2 to 2.8 | |
| Cr | 0.15 to 0.35 | |
| Si | 0 to 0.4 | |
| Fe | 0 to 0.4 | |
| Zn | 0 to 0.1 | |
| Cu | 0 to 0.040 | |
| Mn | 0 to 0.010 | |
| res. | 0 to 0.15 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM B209: Standard Specification for Aluminum and Aluminum-Alloy Sheet and Plate
Aluminum Standards and Data, Aluminum Association Inc., 2013
ASM Specialty Handbook: Aluminum and Aluminum Alloys, J. R. Davis (editor), 1993
CRC Materials Science and Engineering Handbook, 4th ed., James F. Shackelford et al. (editors), 2015