6005-T4 Aluminum
6005-T4 aluminum is 6005 aluminum in the T4 temper. To achieve this temper, the metal is solution heat-treated and naturally aged. It has the second lowest strength and highest ductility compared to the other variants of 6005 aluminum.
The graph bars on the material properties cards below compare 6005-T4 aluminum to: 6000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
68 GPa 9.9 x 106 psi
Elongation at Break
17 %
Fatigue Strength
55 MPa 8.0 x 103 psi
Poisson's Ratio
0.33
Shear Modulus
26 GPa 3.7 x 106 psi
Shear Strength
120 MPa 18 x 103 psi
Tensile Strength: Ultimate (UTS)
200 MPa 29 x 103 psi
Tensile Strength: Yield (Proof)
100 MPa 15 x 103 psi
Thermal Properties
Latent Heat of Fusion
410 J/g
Maximum Temperature: Mechanical
160 °C 320 °F
Melting Completion (Liquidus)
650 °C 1210 °F
Melting Onset (Solidus)
610 °C 1130 °F
Specific Heat Capacity
900 J/kg-K 0.22 BTU/lb-°F
Thermal Conductivity
200 W/m-K 120 BTU/h-ft-°F
Thermal Expansion
23 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
54 % IACS
Electrical Conductivity: Equal Weight (Specific)
180 % IACS
Otherwise Unclassified Properties
Base Metal Price
9.5 % relative
Calomel Potential
-740 mV
Density
2.7 g/cm3 170 lb/ft3
Embodied Carbon
8.3 kg CO2/kg material
Embodied Energy
150 MJ/kg 66 x 103 BTU/lb
Embodied Water
1180 L/kg 140 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
28 MJ/m3
Resilience: Unit (Modulus of Resilience)
77 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
51 points
Strength to Weight: Axial
21 points
Strength to Weight: Bending
28 points
Thermal Diffusivity
83 mm2/s
Thermal Shock Resistance
9.0 points
Alloy Composition
| Al | 97.5 to 99 | |
| Si | 0.6 to 0.9 | |
| Mg | 0.4 to 0.6 | |
| Fe | 0 to 0.35 | |
| Mn | 0 to 0.1 | |
| Cr | 0 to 0.1 | |
| Ti | 0 to 0.1 | |
| Zn | 0 to 0.1 | |
| Cu | 0 to 0.1 | |
| res. | 0 to 0.15 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM B221: Standard Specification for Aluminum and Aluminum-Alloy Extruded Bars, Rods, Wire, Profiles, and Tubes
Advanced Materials in Automotive Engineering, Jason Rowe (editor), 2012
EN 755-2: Aluminium and aluminium alloys. Extruded rod/bar, tube and profiles. Mechanical properties
Aluminum Standards and Data, Aluminum Association Inc., 2013
ASM Specialty Handbook: Aluminum and Aluminum Alloys, J. R. Davis (editor), 1993
EN 573-3: Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products