6182-T6 Aluminum
6182-T6 aluminum is 6182 aluminum in the T6 temper. To achieve this temper, the metal is solution heat-treated and artificially aged until it meets standard mechanical property requirements. The graph bars on the material properties cards below compare 6182-T6 aluminum to: 6000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
70 GPa 10 x 106 psi
Elongation at Break
6.8 %
Fatigue Strength
99 MPa 14 x 103 psi
Poisson's Ratio
0.33
Shear Modulus
26 GPa 3.8 x 106 psi
Shear Strength
190 MPa 27 x 103 psi
Tensile Strength: Ultimate (UTS)
320 MPa 46 x 103 psi
Tensile Strength: Yield (Proof)
270 MPa 39 x 103 psi
Thermal Properties
Latent Heat of Fusion
410 J/g
Maximum Temperature: Mechanical
190 °C 370 °F
Melting Completion (Liquidus)
640 °C 1190 °F
Melting Onset (Solidus)
600 °C 1110 °F
Specific Heat Capacity
900 J/kg-K 0.21 BTU/lb-°F
Thermal Conductivity
160 W/m-K 92 BTU/h-ft-°F
Thermal Expansion
23 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
40 % IACS
Electrical Conductivity: Equal Weight (Specific)
130 % IACS
Otherwise Unclassified Properties
Base Metal Price
9.5 % relative
Density
2.7 g/cm3 170 lb/ft3
Embodied Carbon
8.4 kg CO2/kg material
Embodied Energy
150 MJ/kg 66 x 103 BTU/lb
Embodied Water
1170 L/kg 140 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
21 MJ/m3
Resilience: Unit (Modulus of Resilience)
520 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
50 points
Strength to Weight: Axial
32 points
Strength to Weight: Bending
38 points
Thermal Diffusivity
65 mm2/s
Thermal Shock Resistance
14 points
Alloy Composition
| Al | 95 to 97.9 | |
| Si | 0.9 to 1.3 | |
| Mg | 0.7 to 1.2 | |
| Mn | 0.5 to 1.0 | |
| Fe | 0 to 0.5 | |
| Cr | 0 to 0.25 | |
| Zr | 0.050 to 0.2 | |
| Zn | 0 to 0.2 | |
| Ti | 0 to 0.1 | |
| Cu | 0 to 0.1 | |
| res. | 0 to 0.15 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
Handbook of Aluminum vol. 2: Alloy Production and Materials Manufacturing, George Totten and D. Scott MacKenzie (editors), 2003
EN 755-2: Aluminium and aluminium alloys. Extruded rod/bar, tube and profiles. Mechanical properties
EN 573-3: Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products
CRC Materials Science and Engineering Handbook, 4th ed., James F. Shackelford et al. (editors), 2015