6262-T6 Aluminum
6262-T6 aluminum is 6262 aluminum in the T6 temper. To achieve this temper, the metal is solution heat-treated and artificially aged until it meets standard mechanical property requirements. The graph bars on the material properties cards below compare 6262-T6 aluminum to: 6000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
68 GPa 9.9 x 106 psi
Elongation at Break
10 %
Fatigue Strength
110 MPa 16 x 103 psi
Poisson's Ratio
0.33
Shear Modulus
26 GPa 3.7 x 106 psi
Shear Strength
190 MPa 27 x 103 psi
Tensile Strength: Ultimate (UTS)
320 MPa 46 x 103 psi
Tensile Strength: Yield (Proof)
270 MPa 39 x 103 psi
Thermal Properties
Latent Heat of Fusion
400 J/g
Maximum Temperature: Mechanical
160 °C 330 °F
Melting Completion (Liquidus)
650 °C 1200 °F
Melting Onset (Solidus)
580 °C 1080 °F
Specific Heat Capacity
890 J/kg-K 0.21 BTU/lb-°F
Thermal Conductivity
170 W/m-K 99 BTU/h-ft-°F
Thermal Expansion
23 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
44 % IACS
Electrical Conductivity: Equal Weight (Specific)
140 % IACS
Otherwise Unclassified Properties
Base Metal Price
10 % relative
Density
2.8 g/cm3 180 lb/ft3
Embodied Carbon
8.3 kg CO2/kg material
Embodied Energy
150 MJ/kg 66 x 103 BTU/lb
Embodied Water
1190 L/kg 140 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
31 MJ/m3
Resilience: Unit (Modulus of Resilience)
530 kJ/m3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
48 points
Strength to Weight: Axial
31 points
Strength to Weight: Bending
37 points
Thermal Diffusivity
69 mm2/s
Thermal Shock Resistance
14 points
Alloy Composition
| Al | 94.7 to 97.8 | |
| Mg | 0.8 to 1.2 | |
| Si | 0.4 to 0.8 | |
| Pb | 0.4 to 0.7 | |
| Bi | 0.4 to 0.7 | |
| Fe | 0 to 0.7 | |
| Cu | 0.15 to 0.4 | |
| Zn | 0 to 0.25 | |
| Cr | 0.040 to 0.14 | |
| Mn | 0 to 0.15 | |
| Ti | 0 to 0.15 | |
| res. | 0 to 0.15 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM B483: Standard Specification for Aluminum and Aluminum-Alloy Drawn Tube and Pipe for General Purpose Applications
ASTM B210: Standard Specification for Aluminum and Aluminum-Alloy Drawn Seamless Tubes
ASTM B211: Standard Specification for Aluminum and Aluminum-Alloy Bar, Rod, and Wire
ASTM B221: Standard Specification for Aluminum and Aluminum-Alloy Extruded Bars, Rods, Wire, Profiles, and Tubes
EN 754-2: Aluminium and aluminium alloys. Cold drawn rod/bar and tube. Mechanical properties
EN 755-2: Aluminium and aluminium alloys. Extruded rod/bar, tube and profiles. Mechanical properties
Aluminum Standards and Data, Aluminum Association Inc., 2013
EN 573-3: Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products
Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993