8011A-H16 Aluminum
8011A-H16 aluminum is 8011A aluminum in the H16 temper. To achieve this temper, the metal is strain hardened to a strength that is roughly 3/4 of the way between annealed (O) and full-hard (H18). It has the second lowest ductility compared to the other variants of 8011A aluminum.
The graph bars on the material properties cards below compare 8011A-H16 aluminum to: otherwise unclassified aluminums (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
47
Elastic (Young's, Tensile) Modulus
69 GPa 10 x 106 psi
Elongation at Break
2.3 %
Fatigue Strength
60 MPa 8.7 x 103 psi
Poisson's Ratio
0.33
Shear Modulus
26 GPa 3.8 x 106 psi
Tensile Strength: Ultimate (UTS)
160 MPa 23 x 103 psi
Tensile Strength: Yield (Proof)
150 MPa 21 x 103 psi
Thermal Properties
Latent Heat of Fusion
400 J/g
Maximum Temperature: Mechanical
170 °C 340 °F
Melting Completion (Liquidus)
650 °C 1190 °F
Melting Onset (Solidus)
630 °C 1170 °F
Specific Heat Capacity
900 J/kg-K 0.21 BTU/lb-°F
Thermal Conductivity
210 W/m-K 120 BTU/h-ft-°F
Thermal Expansion
23 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
56 % IACS
Electrical Conductivity: Equal Weight (Specific)
180 % IACS
Otherwise Unclassified Properties
Base Metal Price
9.0 % relative
Density
2.7 g/cm3 170 lb/ft3
Embodied Carbon
8.2 kg CO2/kg material
Embodied Energy
150 MJ/kg 66 x 103 BTU/lb
Embodied Water
1180 L/kg 140 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
3.5 MJ/m3
Resilience: Unit (Modulus of Resilience)
150 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
50 points
Strength to Weight: Axial
16 points
Strength to Weight: Bending
24 points
Thermal Diffusivity
86 mm2/s
Thermal Shock Resistance
7.1 points
Alloy Composition
| Al | 97.5 to 99.1 | |
| Fe | 0.5 to 1.0 | |
| Si | 0.4 to 0.8 | |
| Mn | 0 to 0.1 | |
| Cr | 0 to 0.1 | |
| Zn | 0 to 0.1 | |
| Cu | 0 to 0.1 | |
| Mg | 0 to 0.1 | |
| Ti | 0 to 0.050 | |
| res. | 0 to 0.15 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
Iron in Aluminium Alloys: Impurity and Alloying Element, N. A. Belov et al., 2002
EN 485-2: Aluminium and aluminium alloys. Sheet, strip and plate. Mechanical properties
ISO 6361-2: Wrought aluminium and aluminium alloys - Sheets, strips and plates - Part 2: Mechanical properties
EN 573-3: Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products
Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993