ASTM A372 Grade J Class 70 Steel
ASTM A372 grade J class 70 is ASTM A372 grade J steel in the normalized and tempered condition. ASTM A372 Grade J Class 70 is the ASTM designation for this material. Older literature may refer to this material as Type V Grade 5 Class 70, but this is now discouraged.
The graph bars on the material properties cards below compare ASTM A372 grade J class 70 to: wrought alloy steels in the same category (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
280
Elastic (Young's, Tensile) Modulus
190 GPa 27 x 106 psi
Elongation at Break
20 %
Fatigue Strength
380 MPa 55 x 103 psi
Poisson's Ratio
0.29
Shear Modulus
73 GPa 11 x 106 psi
Shear Strength
570 MPa 83 x 103 psi
Tensile Strength: Ultimate (UTS)
910 MPa 130 x 103 psi
Tensile Strength: Yield (Proof)
550 MPa 80 x 103 psi
Thermal Properties
Latent Heat of Fusion
250 J/g
Maximum Temperature: Mechanical
420 °C 790 °F
Melting Completion (Liquidus)
1460 °C 2660 °F
Melting Onset (Solidus)
1420 °C 2580 °F
Specific Heat Capacity
470 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
44 W/m-K 26 BTU/h-ft-°F
Thermal Expansion
13 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
7.3 % IACS
Electrical Conductivity: Equal Weight (Specific)
8.4 % IACS
Otherwise Unclassified Properties
Base Metal Price
2.4 % relative
Density
7.8 g/cm3 490 lb/ft3
Embodied Carbon
1.5 kg CO2/kg material
Embodied Energy
20 MJ/kg 8.6 x 103 BTU/lb
Embodied Water
51 L/kg 6.1 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
160 MJ/m3
Resilience: Unit (Modulus of Resilience)
810 kJ/m3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
32 points
Strength to Weight: Bending
27 points
Thermal Diffusivity
12 mm2/s
Thermal Shock Resistance
27 points
Alloy Composition
| Fe | 96.7 to 97.8 | |
| Cr | 0.8 to 1.2 | |
| Mn | 0.75 to 1.1 | |
| C | 0.35 to 0.5 | |
| Si | 0.15 to 0.35 | |
| Mo | 0.15 to 0.25 | |
| P | 0 to 0.015 | |
| S | 0 to 0.010 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM A372: Standard Specification for Carbon and Alloy Steel Forgings for Thin-Walled Pressure Vessels
Pressure Vessels: External Pressure Technology, 2nd ed., Carl T. F. Ross, 2011
Manufacture and Uses of Alloy Steels, Henry D. Hibbard, 2005
Steels: Processing, Structure, and Performance, 2nd ed., George Krauss, 2015