ASTM A387 Grade 22 Class 1 Steel
ASTM A387 grade 22 class 1 is ASTM A387 grade 22 steel in the annealed condition. The graph bars on the material properties cards below compare ASTM A387 grade 22 class 1 to: wrought alloy steels in the same category (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
150
Elastic (Young's, Tensile) Modulus
190 GPa 28 x 106 psi
Elongation at Break
21 %
Fatigue Strength
160 MPa 24 x 103 psi
Poisson's Ratio
0.29
Reduction in Area
40 %
Shear Modulus
74 GPa 11 x 106 psi
Shear Strength
300 MPa 44 x 103 psi
Tensile Strength: Ultimate (UTS)
480 MPa 70 x 103 psi
Tensile Strength: Yield (Proof)
230 MPa 34 x 103 psi
Thermal Properties
Latent Heat of Fusion
260 J/g
Maximum Temperature: Mechanical
460 °C 860 °F
Melting Completion (Liquidus)
1470 °C 2680 °F
Melting Onset (Solidus)
1430 °C 2600 °F
Specific Heat Capacity
470 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
40 W/m-K 23 BTU/h-ft-°F
Thermal Expansion
13 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
7.5 % IACS
Electrical Conductivity: Equal Weight (Specific)
8.6 % IACS
Otherwise Unclassified Properties
Base Metal Price
3.8 % relative
Density
7.9 g/cm3 490 lb/ft3
Embodied Carbon
1.7 kg CO2/kg material
Embodied Energy
23 MJ/kg 9.8 x 103 BTU/lb
Embodied Water
58 L/kg 6.9 gal/lb
Common Calculations
PREN (Pitting Resistance)
5.6
Resilience: Ultimate (Unit Rupture Work)
85 MJ/m3
Resilience: Unit (Modulus of Resilience)
140 kJ/m3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
17 points
Strength to Weight: Bending
17 points
Thermal Diffusivity
11 mm2/s
Thermal Shock Resistance
14 points
Alloy Composition
| Fe | 95.1 to 96.8 | |
| Cr | 2.0 to 2.5 | |
| Mo | 0.9 to 1.1 | |
| Mn | 0.3 to 0.6 | |
| Si | 0 to 0.5 | |
| C | 0.050 to 0.15 | |
| P | 0 to 0.025 | |
| S | 0 to 0.025 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM A387: Standard Specification for Pressure Vessel Plates, Alloy Steel, Chromium-Molybdenum
ASTM A182: Standard Specification for Forged or Rolled Alloy and Stainless Steel Pipe Flanges, Forged Fittings, and Valves and Parts for High-Temperature Service
Pressure Vessels: External Pressure Technology, 2nd ed., Carl T. F. Ross, 2011
Properties and Selection: Irons, Steels and High Performance Alloys, ASM Handbook vol. 1, ASM International, 1993
Manufacture and Uses of Alloy Steels, Henry D. Hibbard, 2005
Steels: Processing, Structure, and Performance, 2nd ed., George Krauss, 2015