ASTM A514 Grade S Steel
ASTM A514 grade S is a type of ASTM A514 steel. Cited properties are appropriate for the quenched and tempered condition. The graph bars on the material properties cards below compare ASTM A514 grade S to: wrought alloy steels in the same category (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
250
Elastic (Young's, Tensile) Modulus
190 GPa 27 x 106 psi
Elongation at Break
21 %
Fatigue Strength
540 MPa 78 x 103 psi
Poisson's Ratio
0.29
Shear Modulus
73 GPa 11 x 106 psi
Shear Strength
520 MPa 75 x 103 psi
Tensile Strength: Ultimate (UTS)
830 MPa 120 x 103 psi
Tensile Strength: Yield (Proof)
770 MPa 110 x 103 psi
Thermal Properties
Latent Heat of Fusion
250 J/g
Maximum Temperature: Mechanical
400 °C 760 °F
Melting Completion (Liquidus)
1460 °C 2660 °F
Melting Onset (Solidus)
1420 °C 2590 °F
Specific Heat Capacity
470 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
51 W/m-K 29 BTU/h-ft-°F
Thermal Expansion
13 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
7.2 % IACS
Electrical Conductivity: Equal Weight (Specific)
8.3 % IACS
Otherwise Unclassified Properties
Base Metal Price
2.4 % relative
Density
7.8 g/cm3 490 lb/ft3
Embodied Carbon
1.6 kg CO2/kg material
Embodied Energy
21 MJ/kg 9.2 x 103 BTU/lb
Embodied Water
48 L/kg 5.8 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
170 MJ/m3
Resilience: Unit (Modulus of Resilience)
1590 kJ/m3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
29 points
Strength to Weight: Bending
25 points
Thermal Diffusivity
14 mm2/s
Thermal Shock Resistance
24 points
Alloy Composition
| Fe | 97 to 98.5 | |
| Mn | 1.1 to 1.5 | |
| Mo | 0.1 to 0.6 | |
| Si | 0.15 to 0.45 | |
| C | 0.11 to 0.21 | |
| Nb | 0 to 0.060 | |
| Ti | 0 to 0.060 | |
| V | 0 to 0.060 | |
| P | 0 to 0.030 | |
| S | 0 to 0.020 | |
| B | 0.0010 to 0.0050 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Similar Alloys
Further Reading
ASTM A514: Standard Specification for High-Yield-Strength, Quenched and Tempered Alloy Steel Plate, Suitable for Welding
Properties and Selection: Irons, Steels and High Performance Alloys, ASM Handbook vol. 1, ASM International, 1993
Manufacture and Uses of Alloy Steels, Henry D. Hibbard, 2005
Ferrous Materials: Steel and Cast Iron, Hans Berns and Werner Theisen, 2008
Steels: Processing, Structure, and Performance, 2nd ed., George Krauss, 2015