ASTM A588 Grade A (K11430) HSLA Steel
ASTM A588 grade A is a type of ASTM A588 steel. Cited properties are appropriate for the as-fabricated (no temper or treatment) condition. ASTM A588 Grade A is the ASTM designation for this material. K11430 is the UNS number.
The graph bars on the material properties cards below compare ASTM A588 grade A to: wrought alloy steels in the same category (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
170
Elastic (Young's, Tensile) Modulus
190 GPa 27 x 106 psi
Elongation at Break
22 %
Fatigue Strength
270 MPa 40 x 103 psi
Poisson's Ratio
0.29
Shear Modulus
73 GPa 11 x 106 psi
Shear Strength
350 MPa 51 x 103 psi
Tensile Strength: Ultimate (UTS)
550 MPa 80 x 103 psi
Tensile Strength: Yield (Proof)
390 MPa 56 x 103 psi
Thermal Properties
Latent Heat of Fusion
260 J/g
Maximum Temperature: Mechanical
410 °C 770 °F
Melting Completion (Liquidus)
1460 °C 2650 °F
Melting Onset (Solidus)
1410 °C 2580 °F
Specific Heat Capacity
470 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
44 W/m-K 25 BTU/h-ft-°F
Thermal Expansion
13 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
7.4 % IACS
Electrical Conductivity: Equal Weight (Specific)
8.5 % IACS
Otherwise Unclassified Properties
Base Metal Price
2.3 % relative
Density
7.8 g/cm3 490 lb/ft3
Embodied Carbon
1.6 kg CO2/kg material
Embodied Energy
22 MJ/kg 9.3 x 103 BTU/lb
Embodied Water
51 L/kg 6.0 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
110 MJ/m3
Resilience: Unit (Modulus of Resilience)
400 kJ/m3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
20 points
Strength to Weight: Bending
19 points
Thermal Diffusivity
12 mm2/s
Thermal Shock Resistance
16 points
Alloy Composition
| Fe | 96 to 98.2 | |
| Mn | 0.8 to 1.5 | |
| Cr | 0.4 to 0.65 | |
| Si | 0.3 to 0.65 | |
| Cu | 0.25 to 0.4 | |
| Ni | 0 to 0.4 | |
| C | 0 to 0.19 | |
| V | 0.020 to 0.1 | |
| S | 0 to 0.050 | |
| P | 0 to 0.040 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Similar Alloys
Further Reading
ASTM A588: Standard Specification for High-Strength Low-Alloy Structural Steel, up to 50 ksi [345 MPa] Minimum Yield Point, with Atmospheric Corrosion Resistance
ASTM A588: Standard Specification for High-Strength Low-Alloy Structural Steel with 50 ksi (345 MPa) Minimum Yield Point to 4 in (100 mm) Thick
Properties and Selection: Irons, Steels and High Performance Alloys, ASM Handbook vol. 1, ASM International, 1993
Manufacture and Uses of Alloy Steels, Henry D. Hibbard, 2005
Ferrous Materials: Steel and Cast Iron, Hans Berns and Werner Theisen, 2008
Steels: Processing, Structure, and Performance, 2nd ed., George Krauss, 2015