Annealed 304L Stainless Steel

Annealed AISI 304L is AISI 304L stainless steel in the annealed condition. The graph bars on the material properties cards below compare annealed AISI 304L to: wrought austenitic stainless steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Brinell Hardness

170

Elastic (Young's, Tensile) Modulus

200 GPa 29 x 106 psi

Elongation at Break

42 %

Fatigue Strength

170 MPa 25 x 103 psi

Poisson's Ratio

0.28

Reduction in Area

53 %

Rockwell B Hardness

79

Shear Modulus

77 GPa 11 x 106 psi

Shear Strength

370 MPa 54 x 103 psi

Tensile Strength: Ultimate (UTS)

540 MPa 78 x 103 psi

Tensile Strength: Yield (Proof)

190 MPa 28 x 103 psi

Thermal Properties

Latent Heat of Fusion

290 J/g

Maximum Temperature: Corrosion

420 °C 790 °F

Maximum Temperature: Mechanical

540 °C 1000 °F

Melting Completion (Liquidus)

1450 °C 2640 °F

Melting Onset (Solidus)

1400 °C 2550 °F

Specific Heat Capacity

480 J/kg-K 0.11 BTU/lb-°F

Thermal Conductivity

16 W/m-K 9.2 BTU/h-ft-°F

Thermal Expansion

17 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

2.4 % IACS

Electrical Conductivity: Equal Weight (Specific)

2.7 % IACS

Otherwise Unclassified Properties

Base Metal Price

16 % relative

Calomel Potential

-80 mV

Density

7.8 g/cm3 490 lb/ft3

Embodied Carbon

3.1 kg CO2/kg material

Embodied Energy

44 MJ/kg 19 x 103 BTU/lb

Embodied Water

150 L/kg 18 gal/lb

Common Calculations

PREN (Pitting Resistance)

20

Resilience: Ultimate (Unit Rupture Work)

180 MJ/m3

Resilience: Unit (Modulus of Resilience)

94 kJ/m3

Stiffness to Weight: Axial

14 points

Stiffness to Weight: Bending

25 points

Strength to Weight: Axial

19 points

Strength to Weight: Bending

19 points

Thermal Diffusivity

4.2 mm2/s

Thermal Shock Resistance

12 points

Alloy Composition

Iron (Fe)Fe 65 to 74
Chromium (Cr)Cr 18 to 20
Nickel (Ni)Ni 8.0 to 12
Manganese (Mn)Mn 0 to 2.0
Silicon (Si)Si 0 to 0.75
Nitrogen (N)N 0 to 0.1
Phosphorus (P)P 0 to 0.045
Carbon (C)C 0 to 0.030
Sulfur (S)S 0 to 0.030

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Further Reading

ASTM A493: Standard Specification for Stainless Steel Wire and Wire Rods for Cold Heading and Cold Forging

ASTM A473: Standard Specification for Stainless Steel Forgings

ASTM A479: Standard Specification for Stainless Steel Bars and Shapes for Use in Boilers and Other Pressure Vessels

ASTM A666: Standard Specification for Annealed or Cold-Worked Austenitic Stainless Steel Sheet, Strip, Plate, and Flat Bar

ASTM A182: Standard Specification for Forged or Rolled Alloy and Stainless Steel Pipe Flanges, Forged Fittings, and Valves and Parts for High-Temperature Service

ASTM A276: Standard Specification for Stainless Steel Bars and Shapes

ASTM A240: Standard Specification for Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications

Welding Metallurgy of Stainless Steels, Erich Folkhard et al., 2012

ASTM A959: Standard Guide for Specifying Harmonized Standard Grade Compositions for Wrought Stainless Steels

Corrosion of Austenitic Stainless Steels: Mechanism, Mitigation and Monitoring, H. S. Khatak and B. Raj (editors), 2002