Annealed 440C Stainless Steel
Annealed AISI 440C is AISI 440C stainless steel in the annealed condition. The graph bars on the material properties cards below compare annealed AISI 440C to: wrought martensitic stainless steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
200 GPa 28 x 106 psi
Elongation at Break
14 %
Fatigue Strength
260 MPa 38 x 103 psi
Poisson's Ratio
0.28
Shear Modulus
76 GPa 11 x 106 psi
Shear Strength
430 MPa 63 x 103 psi
Tensile Strength: Ultimate (UTS)
710 MPa 100 x 103 psi
Tensile Strength: Yield (Proof)
450 MPa 65 x 103 psi
Thermal Properties
Latent Heat of Fusion
280 J/g
Maximum Temperature: Corrosion
390 °C 730 °F
Maximum Temperature: Mechanical
870 °C 1600 °F
Melting Completion (Liquidus)
1480 °C 2700 °F
Melting Onset (Solidus)
1370 °C 2500 °F
Specific Heat Capacity
480 J/kg-K 0.12 BTU/lb-°F
Thermal Conductivity
22 W/m-K 13 BTU/h-ft-°F
Thermal Expansion
10 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
2.4 % IACS
Electrical Conductivity: Equal Weight (Specific)
2.8 % IACS
Otherwise Unclassified Properties
Base Metal Price
9.0 % relative
Density
7.7 g/cm3 480 lb/ft3
Embodied Carbon
2.2 kg CO2/kg material
Embodied Energy
31 MJ/kg 13 x 103 BTU/lb
Embodied Water
120 L/kg 14 gal/lb
Common Calculations
PREN (Pitting Resistance)
18
Resilience: Ultimate (Unit Rupture Work)
88 MJ/m3
Resilience: Unit (Modulus of Resilience)
520 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
25 points
Strength to Weight: Axial
26 points
Strength to Weight: Bending
23 points
Thermal Diffusivity
6.0 mm2/s
Thermal Shock Resistance
26 points
Alloy Composition
| Fe | 78 to 83.1 | |
| Cr | 16 to 18 | |
| C | 1.0 to 1.2 | |
| Mn | 0 to 1.0 | |
| Si | 0 to 1.0 | |
| Mo | 0 to 0.75 | |
| P | 0 to 0.040 | |
| S | 0 to 0.015 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM A493: Standard Specification for Stainless Steel Wire and Wire Rods for Cold Heading and Cold Forging
ASTM A276: Standard Specification for Stainless Steel Bars and Shapes
Creep-Resistant Steels, Fujio Abe et al. (editors), 2008
Welding Metallurgy and Weldability of Stainless Steels, John C. Lippold and Damian J. Kotecki, 2005
Advanced Materials in Automotive Engineering, Jason Rowe (editor), 2012
ASTM A959: Standard Guide for Specifying Harmonized Standard Grade Compositions for Wrought Stainless Steels
Properties and Selection: Irons, Steels and High Performance Alloys, ASM Handbook vol. 1, ASM International, 1993
Corrosion of Stainless Steels, A. John Sedriks, 1996
ASM Specialty Handbook: Stainless Steels, J. R. Davis (editor), 1994
Advances in Stainless Steels, Baldev Raj et al. (editors), 2010