Annealed 5130 Chromium Steel
Annealed SAE-AISI 5130 is SAE-AISI 5130 steel in the annealed condition. The graph bars on the material properties cards below compare annealed SAE-AISI 5130 to: SAE-AISI wrought steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
150
Elastic (Young's, Tensile) Modulus
190 GPa 27 x 106 psi
Elongation at Break
22 %
Fatigue Strength
230 MPa 34 x 103 psi
Poisson's Ratio
0.29
Shear Modulus
73 GPa 11 x 106 psi
Shear Strength
310 MPa 46 x 103 psi
Tensile Strength: Ultimate (UTS)
500 MPa 72 x 103 psi
Tensile Strength: Yield (Proof)
330 MPa 48 x 103 psi
Thermal Properties
Latent Heat of Fusion
250 J/g
Maximum Temperature: Mechanical
420 °C 790 °F
Melting Completion (Liquidus)
1460 °C 2660 °F
Melting Onset (Solidus)
1420 °C 2580 °F
Specific Heat Capacity
470 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
45 W/m-K 26 BTU/h-ft-°F
Thermal Expansion
12 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
7.2 % IACS
Electrical Conductivity: Equal Weight (Specific)
8.3 % IACS
Otherwise Unclassified Properties
Base Metal Price
2.2 % relative
Density
7.8 g/cm3 490 lb/ft3
Embodied Carbon
1.4 kg CO2/kg material
Embodied Energy
19 MJ/kg 8.2 x 103 BTU/lb
Embodied Water
50 L/kg 6.0 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
98 MJ/m3
Resilience: Unit (Modulus of Resilience)
290 kJ/m3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
18 points
Strength to Weight: Bending
18 points
Thermal Diffusivity
12 mm2/s
Thermal Shock Resistance
16 points
Alloy Composition
| Fe | 97.2 to 98.1 | |
| Cr | 0.8 to 1.1 | |
| Mn | 0.7 to 0.9 | |
| C | 0.28 to 0.33 | |
| Si | 0.15 to 0.35 | |
| S | 0 to 0.040 | |
| P | 0 to 0.035 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM A752: Standard Specification for General Requirements for Wire Rods and Coarse Round Wire, Alloy Steel
ASTM A322: Standard Specification for Steel Bars, Alloy, Standard Grades
Properties and Selection: Irons, Steels and High Performance Alloys, ASM Handbook vol. 1, ASM International, 1993
ASM Specialty Handbook: Carbon and Alloy Steels, J. R. Davis (editor), 1996
Manufacture and Uses of Alloy Steels, Henry D. Hibbard, 2005
CRC Materials Science and Engineering Handbook, 4th ed., James F. Shackelford et al. (editors), 2015
Steels: Processing, Structure, and Performance, 2nd ed., George Krauss, 2015