Annealed (+A) 1.0033 Steel
EN 1.0033 +A steel is EN 1.0033 steel in the annealed condition. The graph bars on the material properties cards below compare EN 1.0033 +A steel to: wrought carbon or non-alloy steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
86
Elastic (Young's, Tensile) Modulus
190 GPa 27 x 106 psi
Elongation at Break
31 %
Fatigue Strength
120 MPa 17 x 103 psi
Poisson's Ratio
0.29
Shear Modulus
73 GPa 11 x 106 psi
Shear Strength
200 MPa 28 x 103 psi
Tensile Strength: Ultimate (UTS)
300 MPa 43 x 103 psi
Tensile Strength: Yield (Proof)
150 MPa 22 x 103 psi
Thermal Properties
Latent Heat of Fusion
250 J/g
Maximum Temperature: Mechanical
400 °C 750 °F
Melting Completion (Liquidus)
1470 °C 2670 °F
Melting Onset (Solidus)
1420 °C 2600 °F
Specific Heat Capacity
470 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
53 W/m-K 31 BTU/h-ft-°F
Thermal Expansion
12 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
7.0 % IACS
Electrical Conductivity: Equal Weight (Specific)
8.0 % IACS
Otherwise Unclassified Properties
Base Metal Price
1.8 % relative
Density
7.9 g/cm3 490 lb/ft3
Embodied Carbon
1.4 kg CO2/kg material
Embodied Energy
18 MJ/kg 7.8 x 103 BTU/lb
Embodied Water
45 L/kg 5.4 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
78 MJ/m3
Resilience: Unit (Modulus of Resilience)
63 kJ/m3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
10 points
Strength to Weight: Bending
13 points
Thermal Diffusivity
14 mm2/s
Thermal Shock Resistance
9.4 points
Alloy Composition
| Fe | 98.8 to 100 | |
| Mn | 0 to 0.7 | |
| Si | 0 to 0.35 | |
| C | 0 to 0.11 | |
| P | 0 to 0.045 | |
| S | 0 to 0.045 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
EN 10296-1: Welded circular steel tubes for mechanical and general engineering purposes - Technical delivery conditions - Part 1: Non-alloy and alloy steel tubes
Carbon Steel Handbook, D. Gandy, 2007
Ferrous Materials: Steel and Cast Iron, Hans Berns and Werner Theisen, 2008
Steels: Processing, Structure, and Performance, 2nd ed., George Krauss, 2015