Annealed (+A) 1.4029 Stainless Steel
EN 1.4029 +A steel is EN 1.4029 stainless steel in the annealed condition. The graph bars on the material properties cards below compare EN 1.4029 +A steel to: wrought martensitic stainless steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
210
Elastic (Young's, Tensile) Modulus
190 GPa 28 x 106 psi
Elongation at Break
20 %
Fatigue Strength
270 MPa 39 x 103 psi
Poisson's Ratio
0.28
Shear Modulus
76 GPa 11 x 106 psi
Shear Strength
440 MPa 64 x 103 psi
Tensile Strength: Ultimate (UTS)
700 MPa 100 x 103 psi
Tensile Strength: Yield (Proof)
410 MPa 60 x 103 psi
Thermal Properties
Latent Heat of Fusion
270 J/g
Maximum Temperature: Corrosion
390 °C 730 °F
Maximum Temperature: Mechanical
750 °C 1390 °F
Melting Completion (Liquidus)
1440 °C 2620 °F
Melting Onset (Solidus)
1400 °C 2550 °F
Specific Heat Capacity
480 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
30 W/m-K 17 BTU/h-ft-°F
Thermal Expansion
10 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
3.1 % IACS
Electrical Conductivity: Equal Weight (Specific)
3.7 % IACS
Otherwise Unclassified Properties
Base Metal Price
7.0 % relative
Density
7.7 g/cm3 480 lb/ft3
Embodied Carbon
2.0 kg CO2/kg material
Embodied Energy
28 MJ/kg 12 x 103 BTU/lb
Embodied Water
100 L/kg 12 gal/lb
Common Calculations
PREN (Pitting Resistance)
14
Resilience: Ultimate (Unit Rupture Work)
120 MJ/m3
Resilience: Unit (Modulus of Resilience)
440 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
25 points
Strength to Weight: Axial
25 points
Strength to Weight: Bending
23 points
Thermal Diffusivity
8.1 mm2/s
Thermal Shock Resistance
26 points
Alloy Composition
| Fe | 82.8 to 87.6 | |
| Cr | 12 to 13.5 | |
| Mn | 0 to 1.5 | |
| Si | 0 to 1.0 | |
| Mo | 0 to 0.6 | |
| C | 0.25 to 0.32 | |
| S | 0.15 to 0.25 | |
| P | 0 to 0.040 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
Metallic Materials: Physical, Mechanical, and Corrosion Properties, Philip A. Schweitzer, 2003
EN 10088-3: Stainless steels - Part 3: Technical delivery conditions for semi-finished products, bars, rods, wire, sections and bright products of corrosion resisting steels for general purposes
EN 10088-1: Stainless steels - Part 1: List of stainless steels
Welding Metallurgy of Stainless Steels, Erich Folkhard et al., 2012
Corrosion of Stainless Steels, A. John Sedriks, 1996
Advances in Stainless Steels, Baldev Raj et al. (editors), 2010