Annealed Grade 200 Maraging Steel
Annealed 200 maraging steel is grade 200 maraging steel in the annealed condition. The graph bars on the material properties cards below compare annealed 200 maraging steel to: maraging steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Compressive (Crushing) Strength
730 MPa 110 x 103 psi
Elastic (Young's, Tensile) Modulus
190 GPa 28 x 106 psi
Elongation at Break
18 %
Poisson's Ratio
0.3
Rockwell C Hardness
29
Shear Modulus
74 GPa 11 x 106 psi
Shear Strength
600 MPa 87 x 103 psi
Tensile Strength: Ultimate (UTS)
970 MPa 140 x 103 psi
Tensile Strength: Yield (Proof)
690 MPa 100 x 103 psi
Thermal Properties
Latent Heat of Fusion
260 J/g
Melting Completion (Liquidus)
1460 °C 2660 °F
Melting Onset (Solidus)
1420 °C 2580 °F
Specific Heat Capacity
460 J/kg-K 0.11 BTU/lb-°F
Thermal Expansion
12 µm/m-K
Otherwise Unclassified Properties
Base Metal Price
31 % relative
Density
8.2 g/cm3 510 lb/ft3
Embodied Carbon
4.5 kg CO2/kg material
Embodied Energy
59 MJ/kg 26 x 103 BTU/lb
Embodied Water
140 L/kg 16 gal/lb
Common Calculations
PREN (Pitting Resistance)
11
Resilience: Ultimate (Unit Rupture Work)
160 MJ/m3
Resilience: Unit (Modulus of Resilience)
1240 kJ/m3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
23 points
Strength to Weight: Axial
33 points
Strength to Weight: Bending
27 points
Thermal Shock Resistance
29 points
Alloy Composition
| Fe | 67.8 to 71.8 | |
| Ni | 17 to 19 | |
| Co | 8.0 to 9.0 | |
| Mo | 3.0 to 3.5 | |
| Ti | 0.15 to 0.25 | |
| Al | 0.050 to 0.15 | |
| Mn | 0 to 0.1 | |
| Si | 0 to 0.1 | |
| Ca | 0 to 0.050 | |
| C | 0 to 0.030 | |
| Zr | 0 to 0.020 | |
| P | 0 to 0.010 | |
| S | 0 to 0.010 | |
| B | 0 to 0.0030 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
MIL-S-46850D: Steel: Bar, Plate, Sheet, Strip, Forgings, and Extrusions, 18 Percent Nickel Alloy, Maraging, 200 KSI, 250 KSI, 300 KSI, and 350 KSI, High Quality
Maraging Steels: Modelling of Microstructure, Properties and Applications, Wei Sha and Zhanli Guo, 2009
Properties and Selection: Irons, Steels and High Performance Alloys, ASM Handbook vol. 1, ASM International, 1993