Annealed Grade 28 Titanium
Annealed grade 28 titanium is grade 28 titanium in the annealed condition. It has the highest ductility compared to the other variants of grade 28 titanium. The graph bars on the material properties cards below compare annealed grade 28 titanium to: wrought titaniums (top), all titanium alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
110 GPa 15 x 106 psi
Elongation at Break
17 %
Fatigue Strength
350 MPa 51 x 103 psi
Poisson's Ratio
0.32
Reduction in Area
22 %
Shear Modulus
40 GPa 5.8 x 106 psi
Shear Strength
440 MPa 63 x 103 psi
Tensile Strength: Ultimate (UTS)
710 MPa 100 x 103 psi
Tensile Strength: Yield (Proof)
540 MPa 78 x 103 psi
Thermal Properties
Latent Heat of Fusion
410 J/g
Maximum Temperature: Mechanical
330 °C 630 °F
Melting Completion (Liquidus)
1640 °C 2980 °F
Melting Onset (Solidus)
1590 °C 2890 °F
Specific Heat Capacity
550 J/kg-K 0.13 BTU/lb-°F
Thermal Conductivity
8.3 W/m-K 4.8 BTU/h-ft-°F
Thermal Expansion
9.9 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
1.3 % IACS
Electrical Conductivity: Equal Weight (Specific)
2.7 % IACS
Otherwise Unclassified Properties
Base Metal Price
36 % relative
Density
4.5 g/cm3 280 lb/ft3
Embodied Carbon
37 kg CO2/kg material
Embodied Energy
600 MJ/kg 260 x 103 BTU/lb
Embodied Water
370 L/kg 44 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
110 MJ/m3
Resilience: Unit (Modulus of Resilience)
1370 kJ/m3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
35 points
Strength to Weight: Axial
44 points
Strength to Weight: Bending
39 points
Thermal Diffusivity
3.4 mm2/s
Thermal Shock Resistance
48 points
Alloy Composition
| Ti | 92.4 to 95.4 | |
| Al | 2.5 to 3.5 | |
| V | 2.0 to 3.0 | |
| Fe | 0 to 0.25 | |
| Ru | 0.080 to 0.14 | |
| O | 0 to 0.15 | |
| C | 0 to 0.080 | |
| N | 0 to 0.030 | |
| H | 0 to 0.015 | |
| res. | 0 to 0.4 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
Titanium Alloys: Modelling of Microstructure, Properties, and Applications, Wei Sha and Savko Malinov, 2009
ASTM B861: Standard Specification for Titanium and Titanium Alloy Seamless Pipe
ASTM B381: Standard Specification for Titanium and Titanium Alloy Forgings
ASTM B265: Standard Specification for Titanium and Titanium Alloy Strip, Sheet, and Plate
ASTM B348: Standard Specification for Titanium and Titanium Alloy Bars and Billets
Titanium and Titanium Alloys: Fundamentals and Applications, Christoph Leyens and Manfred Peters (editors), 2003
Titanium, 2nd ed., G. Lutjering and J. C. Williams, 2007
Environmental Degradation of Advanced and Traditional Engineering Materials, Lloyd H. Hihara et al., 2014.