Annealed (OS070) C26000 Brass
OS070 C26000 brass is C26000 brass in the OS070 (annealed to 0.070mm grain size) temper. The graph bars on the material properties cards below compare OS070 C26000 brass to: wrought brasses (top), all copper alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
110 GPa 16 x 106 psi
Elongation at Break
59 %
Poisson's Ratio
0.31
Shear Modulus
41 GPa 5.9 x 106 psi
Shear Strength
250 MPa 36 x 103 psi
Tensile Strength: Ultimate (UTS)
330 MPa 48 x 103 psi
Thermal Properties
Latent Heat of Fusion
180 J/g
Maximum Temperature: Mechanical
140 °C 280 °F
Melting Completion (Liquidus)
950 °C 1750 °F
Melting Onset (Solidus)
920 °C 1680 °F
Specific Heat Capacity
390 J/kg-K 0.092 BTU/lb-°F
Thermal Conductivity
120 W/m-K 70 BTU/h-ft-°F
Thermal Expansion
20 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
28 % IACS
Electrical Conductivity: Equal Weight (Specific)
31 % IACS
Otherwise Unclassified Properties
Base Metal Price
25 % relative
Density
8.2 g/cm3 510 lb/ft3
Embodied Carbon
2.7 kg CO2/kg material
Embodied Energy
45 MJ/kg 19 x 103 BTU/lb
Embodied Water
320 L/kg 38 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
6.1 to 420 MJ/m3
Resilience: Unit (Modulus of Resilience)
51 to 1490 kJ/m3
Stiffness to Weight: Axial
7.2 points
Stiffness to Weight: Bending
19 points
Strength to Weight: Axial
11 points
Strength to Weight: Bending
13 points
Thermal Diffusivity
38 mm2/s
Thermal Shock Resistance
11 points
Alloy Composition
| Cu | 68.5 to 71.5 | |
| Zn | 28.1 to 31.5 | |
| Pb | 0 to 0.070 | |
| Fe | 0 to 0.050 | |
| Bi | 0 to 0.0059 | |
| res. | 0 to 0.3 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM B19: Standard Specification for Cartridge Brass Sheet, Strip, Plate, Bar, and Disks
Copper: Its Trade, Manufacture, Use, and Environmental Status, Gunter Joseph, 2001
Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993