Cold Drawn 1046 Carbon Steel
Cold drawn SAE-AISI 1046 is SAE-AISI 1046 steel in the cold worked (strain hardened) condition. It has the highest strength compared to the other variants of SAE-AISI 1046 steel. The graph bars on the material properties cards below compare cold drawn SAE-AISI 1046 to: wrought carbon or non-alloy steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
210
Elastic (Young's, Tensile) Modulus
190 GPa 27 x 106 psi
Elongation at Break
14 %
Fatigue Strength
390 MPa 56 x 103 psi
Poisson's Ratio
0.29
Reduction in Area
39 %
Shear Modulus
72 GPa 11 x 106 psi
Shear Strength
450 MPa 65 x 103 psi
Tensile Strength: Ultimate (UTS)
740 MPa 110 x 103 psi
Tensile Strength: Yield (Proof)
610 MPa 88 x 103 psi
Thermal Properties
Latent Heat of Fusion
250 J/g
Maximum Temperature: Mechanical
400 °C 750 °F
Melting Completion (Liquidus)
1460 °C 2660 °F
Melting Onset (Solidus)
1420 °C 2590 °F
Specific Heat Capacity
470 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
51 W/m-K 30 BTU/h-ft-°F
Thermal Expansion
11 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
11 % IACS
Electrical Conductivity: Equal Weight (Specific)
12 % IACS
Otherwise Unclassified Properties
Base Metal Price
1.8 % relative
Density
7.8 g/cm3 490 lb/ft3
Embodied Carbon
1.4 kg CO2/kg material
Embodied Energy
18 MJ/kg 7.9 x 103 BTU/lb
Embodied Water
46 L/kg 5.5 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
95 MJ/m3
Resilience: Unit (Modulus of Resilience)
990 kJ/m3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
26 points
Strength to Weight: Bending
23 points
Thermal Diffusivity
14 mm2/s
Thermal Shock Resistance
25 points
Alloy Composition
| Fe | 98.4 to 98.9 | |
| Mn | 0.7 to 1.0 | |
| C | 0.43 to 0.5 | |
| S | 0 to 0.050 | |
| P | 0 to 0.040 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
Cold-Formed Steel Structures to the AISI Specification, Gregory J. Hancock et al., 2001
ASTM A29: Standard Specification for Steel Bars, Carbon and Alloy, Hot-Wrought, General Requirements for
Microstructure of Steels and Cast Irons, Madeleine Durand-Charre, 2004
Carbon Steel Handbook, D. Gandy, 2007
ASM Specialty Handbook: Carbon and Alloy Steels, J. R. Davis (editor), 1996
Ferrous Materials: Steel and Cast Iron, Hans Berns and Werner Theisen, 2008
Steels: Processing, Structure, and Performance, 2nd ed., George Krauss, 2015