Cold Drawn 1548 Carbon Steel
Cold drawn SAE-AISI 1548 is SAE-AISI 1548 steel in the cold worked (strain hardened) condition. It has the highest strength compared to the other variants of SAE-AISI 1548 steel. The graph bars on the material properties cards below compare cold drawn SAE-AISI 1548 to: wrought resulfurized carbon steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
250
Elastic (Young's, Tensile) Modulus
190 GPa 27 x 106 psi
Elongation at Break
11 %
Fatigue Strength
430 MPa 62 x 103 psi
Poisson's Ratio
0.29
Reduction in Area
31 %
Shear Modulus
72 GPa 11 x 106 psi
Shear Strength
500 MPa 73 x 103 psi
Tensile Strength: Ultimate (UTS)
830 MPa 120 x 103 psi
Tensile Strength: Yield (Proof)
690 MPa 100 x 103 psi
Thermal Properties
Latent Heat of Fusion
250 J/g
Maximum Temperature: Mechanical
400 °C 750 °F
Melting Completion (Liquidus)
1460 °C 2660 °F
Melting Onset (Solidus)
1420 °C 2580 °F
Specific Heat Capacity
470 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
51 W/m-K 29 BTU/h-ft-°F
Thermal Expansion
12 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
7.1 % IACS
Electrical Conductivity: Equal Weight (Specific)
8.1 % IACS
Otherwise Unclassified Properties
Base Metal Price
1.8 % relative
Density
7.8 g/cm3 490 lb/ft3
Embodied Carbon
1.4 kg CO2/kg material
Embodied Energy
19 MJ/kg 8.0 x 103 BTU/lb
Embodied Water
47 L/kg 5.6 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
90 MJ/m3
Resilience: Unit (Modulus of Resilience)
1280 kJ/m3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
30 points
Strength to Weight: Bending
25 points
Thermal Diffusivity
14 mm2/s
Thermal Shock Resistance
27 points
Alloy Composition
| Fe | 98 to 98.5 | |
| Mn | 1.1 to 1.4 | |
| C | 0.44 to 0.52 | |
| S | 0 to 0.050 | |
| P | 0 to 0.040 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM A29: Standard Specification for Steel Bars, Carbon and Alloy, Hot-Wrought, General Requirements for
Properties and Selection: Irons, Steels and High Performance Alloys, ASM Handbook vol. 1, ASM International, 1993
Carbon Steel Handbook, D. Gandy, 2007
ASM Specialty Handbook: Carbon and Alloy Steels, J. R. Davis (editor), 1996
Ferrous Materials: Steel and Cast Iron, Hans Berns and Werner Theisen, 2008
CRC Materials Science and Engineering Handbook, 4th ed., James F. Shackelford et al. (editors), 2015
Steels: Processing, Structure, and Performance, 2nd ed., George Krauss, 2015