Cold Finished 347 Stainless Steel
Cold finished AISI 347 is AISI 347 stainless steel in the cold worked (strain hardened) condition. The graph bars on the material properties cards below compare cold finished AISI 347 to: wrought austenitic stainless steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
210
Elastic (Young's, Tensile) Modulus
200 GPa 29 x 106 psi
Elongation at Break
34 %
Fatigue Strength
270 MPa 40 x 103 psi
Poisson's Ratio
0.28
Shear Modulus
77 GPa 11 x 106 psi
Shear Strength
460 MPa 67 x 103 psi
Tensile Strength: Ultimate (UTS)
690 MPa 100 x 103 psi
Tensile Strength: Yield (Proof)
350 MPa 50 x 103 psi
Thermal Properties
Latent Heat of Fusion
290 J/g
Maximum Temperature: Corrosion
480 °C 900 °F
Maximum Temperature: Mechanical
870 °C 1600 °F
Melting Completion (Liquidus)
1430 °C 2600 °F
Melting Onset (Solidus)
1400 °C 2550 °F
Specific Heat Capacity
480 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
16 W/m-K 9.3 BTU/h-ft-°F
Thermal Expansion
17 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
2.4 % IACS
Electrical Conductivity: Equal Weight (Specific)
2.7 % IACS
Otherwise Unclassified Properties
Base Metal Price
19 % relative
Calomel Potential
-80 mV
Density
7.8 g/cm3 490 lb/ft3
Embodied Carbon
3.6 kg CO2/kg material
Embodied Energy
52 MJ/kg 22 x 103 BTU/lb
Embodied Water
150 L/kg 17 gal/lb
Common Calculations
PREN (Pitting Resistance)
18
Resilience: Ultimate (Unit Rupture Work)
190 MJ/m3
Resilience: Unit (Modulus of Resilience)
310 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
25 points
Strength to Weight: Axial
25 points
Strength to Weight: Bending
22 points
Thermal Diffusivity
4.3 mm2/s
Thermal Shock Resistance
15 points
Alloy Composition
| Fe | 64.1 to 74 | |
| Cr | 17 to 19 | |
| Ni | 9.0 to 13 | |
| Mn | 0 to 2.0 | |
| Nb | 0 to 1.0 | |
| Si | 0 to 0.75 | |
| C | 0 to 0.080 | |
| P | 0 to 0.045 | |
| S | 0 to 0.030 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM A182: Standard Specification for Forged or Rolled Alloy and Stainless Steel Pipe Flanges, Forged Fittings, and Valves and Parts for High-Temperature Service
ASTM A276: Standard Specification for Stainless Steel Bars and Shapes
Welding Metallurgy and Weldability of Stainless Steels, John C. Lippold and Damian J. Kotecki, 2005
ASTM A959: Standard Guide for Specifying Harmonized Standard Grade Compositions for Wrought Stainless Steels
Corrosion of Austenitic Stainless Steels: Mechanism, Mitigation and Monitoring, H. S. Khatak and B. Raj (editors), 2002
Pressure Vessels: External Pressure Technology, 2nd ed., Carl T. F. Ross, 2011
Austenitic Stainless Steels: Microstructure and Mechanical Properties, P. Marshall, 1984
ASM Specialty Handbook: Stainless Steels, J. R. Davis (editor), 1994
Advances in Stainless Steels, Baldev Raj et al. (editors), 2010