Cold Finished 4130 Cr-Mo Steel
Cold finished SAE-AISI 4130 is SAE-AISI 4130 steel in the cold worked (strain hardened) condition. It has the lowest ductility compared to the other variants of SAE-AISI 4130 steel. The graph bars on the material properties cards below compare cold finished SAE-AISI 4130 to: SAE-AISI wrought steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
210
Elastic (Young's, Tensile) Modulus
190 GPa 27 x 106 psi
Elongation at Break
13 %
Fatigue Strength
370 MPa 53 x 103 psi
Poisson's Ratio
0.29
Shear Modulus
73 GPa 11 x 106 psi
Shear Strength
420 MPa 60 x 103 psi
Tensile Strength: Ultimate (UTS)
690 MPa 100 x 103 psi
Tensile Strength: Yield (Proof)
580 MPa 84 x 103 psi
Thermal Properties
Latent Heat of Fusion
250 J/g
Maximum Temperature: Mechanical
420 °C 790 °F
Melting Completion (Liquidus)
1460 °C 2660 °F
Melting Onset (Solidus)
1420 °C 2590 °F
Specific Heat Capacity
470 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
43 W/m-K 25 BTU/h-ft-°F
Thermal Expansion
13 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
7.2 % IACS
Electrical Conductivity: Equal Weight (Specific)
8.3 % IACS
Otherwise Unclassified Properties
Base Metal Price
2.4 % relative
Density
7.8 g/cm3 490 lb/ft3
Embodied Carbon
1.5 kg CO2/kg material
Embodied Energy
20 MJ/kg 8.4 x 103 BTU/lb
Embodied Water
50 L/kg 6.0 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
83 MJ/m3
Resilience: Unit (Modulus of Resilience)
900 kJ/m3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
24 points
Strength to Weight: Bending
22 points
Thermal Diffusivity
12 mm2/s
Thermal Shock Resistance
20 points
Alloy Composition
| Fe | 97.3 to 98.2 | |
| Cr | 0.8 to 1.1 | |
| Mn | 0.4 to 0.6 | |
| C | 0.28 to 0.33 | |
| Si | 0.15 to 0.35 | |
| Mo | 0.15 to 0.25 | |
| S | 0 to 0.040 | |
| P | 0 to 0.035 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM A322: Standard Specification for Steel Bars, Alloy, Standard Grades
ASM Specialty Handbook: Carbon and Alloy Steels, J. R. Davis (editor), 1996
Manufacture and Uses of Alloy Steels, Henry D. Hibbard, 2005
Steels: Processing, Structure, and Performance, 2nd ed., George Krauss, 2015