Conditioned 30% Carbon Fiber (30 CF) PA 6
Conditioned 30 CF PA 6 is a grade of PA 6. It has the second lowest ductility compared to the other variants of PA 6. The graph bars on the material properties cards below compare conditioned 30 CF PA 6 to: polyamide plastics (top), all thermoplastics (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
11 GPa 1.6 x 106 psi
Elongation at Break
3.0 %
Flexural Modulus
5.0 GPa 0.73 x 106 psi
Flexural Strength
140 MPa 20 x 103 psi
Tensile Strength: Ultimate (UTS)
150 MPa 22 x 103 psi
Other Material Properties
Glass Transition Temperature
40 °C 100 °F
Limiting Oxygen Index (LOI)
24 %
Maximum Temperature: Autoignition
430 °C 810 °F
Maximum Temperature: Decomposition
430 °C 800 °F
Melting Onset (Solidus)
230 °C 450 °F
Followup Questions
Further Reading
SPI Plastics Engineering Handbook of the Society of the Plastics Industry, Inc., 5th ed., Michael L. Berins (editor), 2000
Modern Plastics Handbook, Charles A. Harper (editor), 1999
Plastics Materials, 7th ed., J. A. Brydson, 1999