EN 1.4584 (GX2NiCrMoCu25-20-5) Cast Stainless Steel
EN 1.4584 stainless steel is an austenitic stainless steel formulated for casting. Cited properties are appropriate for the solution annealed (AT) condition. 1.4584 is the EN numeric designation for this material. GX2NiCrMoCu25-20-5 is the EN chemical designation.
It has a fairly high thermal conductivity among cast austenitic stainless steels. In addition, it has a moderately high base cost and a moderately high embodied energy.
The graph bars on the material properties cards below compare EN 1.4584 stainless steel to: cast austenitic stainless steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
150
Elastic (Young's, Tensile) Modulus
200 GPa 29 x 106 psi
Elongation at Break
34 %
Fatigue Strength
170 MPa 24 x 103 psi
Impact Strength: V-Notched Charpy
67 J 50 ft-lb
Poisson's Ratio
0.28
Shear Modulus
79 GPa 11 x 106 psi
Tensile Strength: Ultimate (UTS)
500 MPa 73 x 103 psi
Tensile Strength: Yield (Proof)
210 MPa 31 x 103 psi
Thermal Properties
Latent Heat of Fusion
300 J/g
Maximum Temperature: Corrosion
420 °C 800 °F
Maximum Temperature: Mechanical
1100 °C 2010 °F
Melting Completion (Liquidus)
1440 °C 2620 °F
Melting Onset (Solidus)
1390 °C 2530 °F
Specific Heat Capacity
460 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
17 W/m-K 9.8 BTU/h-ft-°F
Thermal Expansion
15 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
1.7 % IACS
Electrical Conductivity: Equal Weight (Specific)
1.9 % IACS
Otherwise Unclassified Properties
Base Metal Price
31 % relative
Density
8.1 g/cm3 500 lb/ft3
Embodied Carbon
5.7 kg CO2/kg material
Embodied Energy
78 MJ/kg 34 x 103 BTU/lb
Embodied Water
200 L/kg 24 gal/lb
Common Calculations
PREN (Pitting Resistance)
36
Resilience: Ultimate (Unit Rupture Work)
140 MJ/m3
Resilience: Unit (Modulus of Resilience)
110 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
17 points
Strength to Weight: Bending
17 points
Thermal Diffusivity
4.5 mm2/s
Thermal Shock Resistance
12 points
Alloy Composition
Among cast stainless steels, the composition of EN 1.4584 stainless steel is notable for containing comparatively high amounts of nickel (Ni) and molybdenum (Mo). Nickel is primarily used to achieve a specific microstructure. In addition, it has a beneficial effect on mechanical properties and certain types of corrosion. Molybdenum is used to facilitate tempering. In addition, it offers modest bonuses to a wide range of material properties.
| Fe | 41.7 to 52 | |
| Ni | 24 to 26 | |
| Cr | 19 to 21 | |
| Mo | 4.0 to 5.0 | |
| Cu | 1.0 to 3.0 | |
| Mn | 0 to 2.0 | |
| Si | 0 to 1.0 | |
| N | 0 to 0.2 | |
| P | 0 to 0.035 | |
| C | 0 to 0.025 | |
| S | 0 to 0.020 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Similar Alloys
Further Reading
EN 10283: Corrosion resistant steel castings
Austenitic Stainless Steels: Microstructure and Mechanical Properties, P. Marshall, 1984
Corrosion of Stainless Steels, A. John Sedriks, 1996
Advances in Stainless Steels, Baldev Raj et al. (editors), 2010