EN AC-42100-T64 Cast Aluminum
EN AC-42100-T64 is EN AC-42100 aluminum in the T64 temper. To achieve this temper, the metal is solution heat-treated and artificially underaged. The degree of underaging is different from T61 and T65.
The graph bars on the material properties cards below compare EN AC-42100-T64 to: Euronorm (EN) cast aluminums (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
91
Elastic (Young's, Tensile) Modulus
70 GPa 10 x 106 psi
Elongation at Break
9.0 %
Fatigue Strength
82 MPa 12 x 103 psi
Poisson's Ratio
0.33
Shear Modulus
26 GPa 3.8 x 106 psi
Tensile Strength: Ultimate (UTS)
280 MPa 41 x 103 psi
Tensile Strength: Yield (Proof)
210 MPa 30 x 103 psi
Thermal Properties
Latent Heat of Fusion
500 J/g
Maximum Temperature: Mechanical
170 °C 340 °F
Melting Completion (Liquidus)
610 °C 1130 °F
Melting Onset (Solidus)
600 °C 1120 °F
Specific Heat Capacity
910 J/kg-K 0.22 BTU/lb-°F
Thermal Conductivity
150 W/m-K 89 BTU/h-ft-°F
Thermal Expansion
22 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
41 % IACS
Electrical Conductivity: Equal Weight (Specific)
140 % IACS
Otherwise Unclassified Properties
Base Metal Price
9.5 % relative
Density
2.6 g/cm3 160 lb/ft3
Embodied Carbon
8.0 kg CO2/kg material
Embodied Energy
150 MJ/kg 64 x 103 BTU/lb
Embodied Water
1110 L/kg 130 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
23 MJ/m3
Resilience: Unit (Modulus of Resilience)
300 kJ/m3
Stiffness to Weight: Axial
15 points
Stiffness to Weight: Bending
53 points
Strength to Weight: Axial
30 points
Strength to Weight: Bending
37 points
Thermal Diffusivity
66 mm2/s
Thermal Shock Resistance
13 points
Alloy Composition
| Al | 91.3 to 93.3 | |
| Si | 6.5 to 7.5 | |
| Mg | 0.25 to 0.45 | |
| Ti | 0 to 0.25 | |
| Fe | 0 to 0.19 | |
| Mn | 0 to 0.1 | |
| Zn | 0 to 0.070 | |
| Cu | 0 to 0.050 | |
| res. | 0 to 0.1 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
EN 1706: Aluminium and aluminium alloys. Castings. Chemical composition and mechanical properties
Handbook of Aluminum Bonding Technology and Data, J. D. Minford, 1993