EN AC-43300-T6 Cast Aluminum
EN AC-43300-T6 is EN AC-43300 aluminum in the T6 temper. To achieve this temper, the metal is solution heat-treated and artificially aged until it meets standard mechanical property requirements. The graph bars on the material properties cards below compare EN AC-43300-T6 to: Euronorm (EN) cast aluminums (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
94
Elastic (Young's, Tensile) Modulus
71 GPa 10 x 106 psi
Elongation at Break
3.4 %
Fatigue Strength
76 MPa 11 x 103 psi
Poisson's Ratio
0.33
Shear Modulus
27 GPa 3.9 x 106 psi
Tensile Strength: Ultimate (UTS)
290 MPa 42 x 103 psi
Tensile Strength: Yield (Proof)
230 MPa 33 x 103 psi
Thermal Properties
Latent Heat of Fusion
540 J/g
Maximum Temperature: Mechanical
170 °C 340 °F
Melting Completion (Liquidus)
600 °C 1110 °F
Melting Onset (Solidus)
590 °C 1100 °F
Specific Heat Capacity
910 J/kg-K 0.22 BTU/lb-°F
Thermal Conductivity
140 W/m-K 79 BTU/h-ft-°F
Thermal Expansion
22 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
40 % IACS
Electrical Conductivity: Equal Weight (Specific)
140 % IACS
Otherwise Unclassified Properties
Base Metal Price
9.5 % relative
Density
2.5 g/cm3 160 lb/ft3
Embodied Carbon
7.9 kg CO2/kg material
Embodied Energy
150 MJ/kg 63 x 103 BTU/lb
Embodied Water
1080 L/kg 130 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
9.1 MJ/m3
Resilience: Unit (Modulus of Resilience)
370 kJ/m3
Stiffness to Weight: Axial
15 points
Stiffness to Weight: Bending
54 points
Strength to Weight: Axial
32 points
Strength to Weight: Bending
38 points
Thermal Diffusivity
59 mm2/s
Thermal Shock Resistance
14 points
Alloy Composition
| Al | 88.9 to 90.8 | |
| Si | 9.0 to 10 | |
| Mg | 0.25 to 0.45 | |
| Fe | 0 to 0.19 | |
| Ti | 0 to 0.15 | |
| Mn | 0 to 0.1 | |
| Zn | 0 to 0.070 | |
| Cu | 0 to 0.050 | |
| res. | 0 to 0.1 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
EN 1706: Aluminium and aluminium alloys. Castings. Chemical composition and mechanical properties
Handbook of Aluminum vol. 2: Alloy Production and Materials Manufacturing, George Totten and D. Scott MacKenzie (editors), 2003