Extra-Hard (H06) C53400 Bronze
H06 C53400 bronze is C53400 bronze in the H06 (extra hard) temper. The graph bars on the material properties cards below compare H06 C53400 bronze to: wrought bronzes (top), all copper alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
110 GPa 16 x 106 psi
Poisson's Ratio
0.34
Rockwell B Hardness
90
Rockwell Superficial 30T Hardness
77
Shear Modulus
42 GPa 6.0 x 106 psi
Tensile Strength: Ultimate (UTS)
630 MPa 92 x 103 psi
Thermal Properties
Latent Heat of Fusion
200 J/g
Maximum Temperature: Mechanical
180 °C 360 °F
Melting Completion (Liquidus)
1050 °C 1920 °F
Melting Onset (Solidus)
950 °C 1750 °F
Specific Heat Capacity
380 J/kg-K 0.090 BTU/lb-°F
Thermal Conductivity
69 W/m-K 40 BTU/h-ft-°F
Thermal Expansion
18 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
15 % IACS
Electrical Conductivity: Equal Weight (Specific)
15 % IACS
Otherwise Unclassified Properties
Base Metal Price
32 % relative
Density
8.9 g/cm3 550 lb/ft3
Embodied Carbon
3.0 kg CO2/kg material
Embodied Energy
49 MJ/kg 21 x 103 BTU/lb
Embodied Water
350 L/kg 41 gal/lb
Common Calculations
Stiffness to Weight: Axial
7.0 points
Stiffness to Weight: Bending
18 points
Strength to Weight: Axial
20 points
Strength to Weight: Bending
18 points
Thermal Diffusivity
21 mm2/s
Thermal Shock Resistance
23 points
Alloy Composition
| Cu | 91.8 to 95.7 | |
| Sn | 3.5 to 5.8 | |
| Pb | 0.8 to 1.2 | |
| P | 0.030 to 0.35 | |
| Zn | 0 to 0.3 | |
| Fe | 0 to 0.1 | |
| res. | 0 to 0.5 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM B103: Standard Specification for Phosphor Bronze Plate, Sheet, Strip, and Rolled Bar
ASM Specialty Handbook: Copper and Copper Alloys, J. R. Davis (editor), 2001