Extra-Hard (H06) C61500 Bronze
H06 C61500 bronze is C61500 bronze in the H06 (extra hard) temper. It has the second highest strength and second lowest ductility compared to the other variants of C61500 bronze. The graph bars on the material properties cards below compare H06 C61500 bronze to: wrought bronzes (top), all copper alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
110 GPa 16 x 106 psi
Elongation at Break
4.0 %
Poisson's Ratio
0.34
Rockwell Superficial 30T Hardness
84
Shear Modulus
42 GPa 6.1 x 106 psi
Shear Strength
540 MPa 78 x 103 psi
Tensile Strength: Ultimate (UTS)
930 MPa 140 x 103 psi
Tensile Strength: Yield (Proof)
690 MPa 100 x 103 psi
Thermal Properties
Latent Heat of Fusion
220 J/g
Maximum Temperature: Mechanical
220 °C 420 °F
Melting Completion (Liquidus)
1040 °C 1900 °F
Melting Onset (Solidus)
1030 °C 1890 °F
Specific Heat Capacity
430 J/kg-K 0.1 BTU/lb-°F
Thermal Conductivity
58 W/m-K 34 BTU/h-ft-°F
Thermal Expansion
18 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
13 % IACS
Electrical Conductivity: Equal Weight (Specific)
13 % IACS
Otherwise Unclassified Properties
Base Metal Price
29 % relative
Density
8.4 g/cm3 530 lb/ft3
Embodied Carbon
3.2 kg CO2/kg material
Embodied Energy
52 MJ/kg 22 x 103 BTU/lb
Embodied Water
380 L/kg 45 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
34 MJ/m3
Resilience: Unit (Modulus of Resilience)
2100 kJ/m3
Stiffness to Weight: Axial
7.5 points
Stiffness to Weight: Bending
19 points
Strength to Weight: Axial
31 points
Strength to Weight: Bending
25 points
Thermal Diffusivity
16 mm2/s
Thermal Shock Resistance
33 points
Alloy Composition
| Cu | 89 to 90.5 | |
| Al | 7.7 to 8.3 | |
| Ni | 1.8 to 2.2 | |
| Pb | 0 to 0.015 | |
| res. | 0 to 0.5 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
CRC Materials Science and Engineering Handbook, 4th ed., James F. Shackelford et al. (editors), 2015