Full-Hard (H04) C36000 Brass
H04 C36000 brass is C36000 brass in the H04 (full hard) temper. It has the highest strength and lowest ductility compared to the other variants of C36000 brass. The graph bars on the material properties cards below compare H04 C36000 brass to: wrought brasses (top), all copper alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
100 GPa 15 x 106 psi
Elongation at Break
5.8 %
Poisson's Ratio
0.31
Shear Modulus
39 GPa 5.7 x 106 psi
Shear Strength
310 MPa 45 x 103 psi
Tensile Strength: Ultimate (UTS)
530 MPa 77 x 103 psi
Tensile Strength: Yield (Proof)
260 MPa 38 x 103 psi
Thermal Properties
Latent Heat of Fusion
170 J/g
Maximum Temperature: Mechanical
120 °C 250 °F
Melting Completion (Liquidus)
900 °C 1650 °F
Melting Onset (Solidus)
890 °C 1630 °F
Specific Heat Capacity
380 J/kg-K 0.090 BTU/lb-°F
Thermal Conductivity
120 W/m-K 67 BTU/h-ft-°F
Thermal Expansion
21 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
26 % IACS
Electrical Conductivity: Equal Weight (Specific)
29 % IACS
Otherwise Unclassified Properties
Base Metal Price
23 % relative
Density
8.2 g/cm3 510 lb/ft3
Embodied Carbon
2.6 kg CO2/kg material
Embodied Energy
45 MJ/kg 19 x 103 BTU/lb
Embodied Water
320 L/kg 38 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
25 MJ/m3
Resilience: Unit (Modulus of Resilience)
340 kJ/m3
Stiffness to Weight: Axial
7.0 points
Stiffness to Weight: Bending
19 points
Strength to Weight: Axial
18 points
Strength to Weight: Bending
18 points
Thermal Diffusivity
37 mm2/s
Thermal Shock Resistance
18 points
Alloy Composition
| Cu | 60 to 63 | |
| Zn | 32.5 to 37.5 | |
| Pb | 2.5 to 3.7 | |
| Fe | 0 to 0.35 | |
| res. | 0 to 0.5 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM B16: Standard Specification for Free-Cutting Brass Rod, Bar and Shapes for Use in Screw Machines
Copper: Its Trade, Manufacture, Use, and Environmental Status, Gunter Joseph, 2001
Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993