H1000 Hardened S17600 Stainless Steel
H1000 hardened S17600 stainless steel is S17600 stainless steel in the hardened (H) condition. The graph bars on the material properties cards below compare H1000 hardened S17600 stainless steel to: wrought precipitation-hardening stainless steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
390
Elastic (Young's, Tensile) Modulus
200 GPa 28 x 106 psi
Elongation at Break
9.1 %
Fatigue Strength
640 MPa 93 x 103 psi
Poisson's Ratio
0.28
Reduction in Area
34 %
Rockwell C Hardness
42
Shear Modulus
76 GPa 11 x 106 psi
Shear Strength
840 MPa 120 x 103 psi
Tensile Strength: Ultimate (UTS)
1410 MPa 210 x 103 psi
Tensile Strength: Yield (Proof)
1230 MPa 180 x 103 psi
Thermal Properties
Latent Heat of Fusion
290 J/g
Maximum Temperature: Corrosion
550 °C 1030 °F
Maximum Temperature: Mechanical
890 °C 1630 °F
Melting Completion (Liquidus)
1430 °C 2610 °F
Melting Onset (Solidus)
1390 °C 2530 °F
Specific Heat Capacity
480 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
15 W/m-K 8.9 BTU/h-ft-°F
Thermal Expansion
11 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
2.3 % IACS
Electrical Conductivity: Equal Weight (Specific)
2.7 % IACS
Otherwise Unclassified Properties
Base Metal Price
13 % relative
Density
7.8 g/cm3 480 lb/ft3
Embodied Carbon
2.9 kg CO2/kg material
Embodied Energy
42 MJ/kg 18 x 103 BTU/lb
Embodied Water
130 L/kg 16 gal/lb
Common Calculations
PREN (Pitting Resistance)
17
Resilience: Ultimate (Unit Rupture Work)
120 MJ/m3
Resilience: Unit (Modulus of Resilience)
3880 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
25 points
Strength to Weight: Axial
51 points
Strength to Weight: Bending
36 points
Thermal Diffusivity
4.1 mm2/s
Thermal Shock Resistance
47 points
Alloy Composition
| Fe | 71.3 to 77.6 | |
| Cr | 16 to 17.5 | |
| Ni | 6.0 to 7.5 | |
| Ti | 0.4 to 1.2 | |
| Mn | 0 to 1.0 | |
| Si | 0 to 1.0 | |
| Al | 0 to 0.4 | |
| C | 0 to 0.080 | |
| P | 0 to 0.040 | |
| S | 0 to 0.030 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM A564: Standard Specification for Hot-Rolled and Cold-Finished Age-Hardening Stainless Steel Bars and Shapes
ASTM A959: Standard Guide for Specifying Harmonized Standard Grade Compositions for Wrought Stainless Steels
Corrosion of Stainless Steels, A. John Sedriks, 1996
ASM Specialty Handbook: Stainless Steels, J. R. Davis (editor), 1994
Advances in Stainless Steels, Baldev Raj et al. (editors), 2010