H1025 Hardened S13800 Stainless Steel
H1025 hardened S13800 stainless steel is S13800 stainless steel in the hardened (H) condition. The graph bars on the material properties cards below compare H1025 hardened S13800 stainless steel to: wrought precipitation-hardening stainless steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
430
Elastic (Young's, Tensile) Modulus
200 GPa 28 x 106 psi
Elongation at Break
13 %
Fatigue Strength
760 MPa 110 x 103 psi
Poisson's Ratio
0.28
Reduction in Area
50 %
Rockwell C Hardness
47
Shear Modulus
77 GPa 11 x 106 psi
Shear Strength
880 MPa 130 x 103 psi
Tensile Strength: Ultimate (UTS)
1460 MPa 210 x 103 psi
Tensile Strength: Yield (Proof)
1360 MPa 200 x 103 psi
Thermal Properties
Latent Heat of Fusion
280 J/g
Maximum Temperature: Corrosion
390 °C 740 °F
Maximum Temperature: Mechanical
810 °C 1490 °F
Melting Completion (Liquidus)
1450 °C 2650 °F
Melting Onset (Solidus)
1410 °C 2570 °F
Specific Heat Capacity
470 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
16 W/m-K 9.3 BTU/h-ft-°F
Thermal Expansion
11 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
2.3 % IACS
Electrical Conductivity: Equal Weight (Specific)
2.6 % IACS
Otherwise Unclassified Properties
Base Metal Price
15 % relative
Density
7.9 g/cm3 490 lb/ft3
Embodied Carbon
3.4 kg CO2/kg material
Embodied Energy
46 MJ/kg 20 x 103 BTU/lb
Embodied Water
140 L/kg 16 gal/lb
Common Calculations
PREN (Pitting Resistance)
21
Resilience: Ultimate (Unit Rupture Work)
180 MJ/m3
Resilience: Unit (Modulus of Resilience)
4680 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
25 points
Strength to Weight: Axial
52 points
Strength to Weight: Bending
36 points
Thermal Diffusivity
4.3 mm2/s
Thermal Shock Resistance
49 points
Alloy Composition
| Fe | 73.6 to 77.3 | |
| Cr | 12.3 to 13.2 | |
| Ni | 7.5 to 8.5 | |
| Mo | 2.0 to 3.0 | |
| Al | 0.9 to 1.4 | |
| Mn | 0 to 0.2 | |
| Si | 0 to 0.1 | |
| C | 0 to 0.050 | |
| P | 0 to 0.010 | |
| N | 0 to 0.010 | |
| S | 0 to 0.0080 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM A564: Standard Specification for Hot-Rolled and Cold-Finished Age-Hardening Stainless Steel Bars and Shapes
ASTM A959: Standard Guide for Specifying Harmonized Standard Grade Compositions for Wrought Stainless Steels
Corrosion of Stainless Steels, A. John Sedriks, 1996
ASM Specialty Handbook: Stainless Steels, J. R. Davis (editor), 1994
Advances in Stainless Steels, Baldev Raj et al. (editors), 2010