Half-Hard 201 Stainless Steel
Half-hard AISI 201 is AISI 201 stainless steel in the half-hard temper. The graph bars on the material properties cards below compare half-hard AISI 201 to: wrought austenitic stainless steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
360
Elastic (Young's, Tensile) Modulus
200 GPa 29 x 106 psi
Elongation at Break
21 %
Fatigue Strength
550 MPa 80 x 103 psi
Poisson's Ratio
0.28
Shear Modulus
77 GPa 11 x 106 psi
Shear Strength
740 MPa 110 x 103 psi
Tensile Strength: Ultimate (UTS)
1180 MPa 170 x 103 psi
Tensile Strength: Yield (Proof)
850 MPa 120 x 103 psi
Thermal Properties
Latent Heat of Fusion
280 J/g
Maximum Temperature: Corrosion
410 °C 770 °F
Maximum Temperature: Mechanical
880 °C 1620 °F
Melting Completion (Liquidus)
1410 °C 2570 °F
Melting Onset (Solidus)
1370 °C 2500 °F
Specific Heat Capacity
480 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
15 W/m-K 8.7 BTU/h-ft-°F
Thermal Expansion
17 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
2.5 % IACS
Electrical Conductivity: Equal Weight (Specific)
2.9 % IACS
Otherwise Unclassified Properties
Base Metal Price
12 % relative
Density
7.7 g/cm3 480 lb/ft3
Embodied Carbon
2.6 kg CO2/kg material
Embodied Energy
38 MJ/kg 16 x 103 BTU/lb
Embodied Water
140 L/kg 17 gal/lb
Common Calculations
PREN (Pitting Resistance)
19
Resilience: Ultimate (Unit Rupture Work)
220 MJ/m3
Resilience: Unit (Modulus of Resilience)
1840 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
25 points
Strength to Weight: Axial
43 points
Strength to Weight: Bending
32 points
Thermal Diffusivity
4.0 mm2/s
Thermal Shock Resistance
26 points
Alloy Composition
| Fe | 67.5 to 75 | |
| Cr | 16 to 18 | |
| Mn | 5.5 to 7.5 | |
| Ni | 3.5 to 5.5 | |
| Si | 0 to 1.0 | |
| N | 0 to 0.25 | |
| C | 0 to 0.15 | |
| P | 0 to 0.060 | |
| S | 0 to 0.030 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM A666: Standard Specification for Annealed or Cold-Worked Austenitic Stainless Steel Sheet, Strip, Plate, and Flat Bar
ASTM A240: Standard Specification for Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications
ASTM A959: Standard Guide for Specifying Harmonized Standard Grade Compositions for Wrought Stainless Steels
Corrosion of Austenitic Stainless Steels: Mechanism, Mitigation and Monitoring, H. S. Khatak and B. Raj (editors), 2002
Austenitic Stainless Steels: Microstructure and Mechanical Properties, P. Marshall, 1984
ASM Specialty Handbook: Stainless Steels, J. R. Davis (editor), 1994
Advances in Stainless Steels, Baldev Raj et al. (editors), 2010