Half-Hard (H02) C19400 Copper
H02 C19400 copper is C19400 copper in the H02 (half hard) temper. The graph bars on the material properties cards below compare H02 C19400 copper to: wrought coppers (top), all copper alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
120 GPa 17 x 106 psi
Elongation at Break
14 %
Poisson's Ratio
0.34
Rockwell B Hardness
60
Rockwell Superficial 30T Hardness
59
Shear Modulus
44 GPa 6.4 x 106 psi
Shear Strength
240 MPa 35 x 103 psi
Tensile Strength: Ultimate (UTS)
400 MPa 58 x 103 psi
Tensile Strength: Yield (Proof)
310 MPa 45 x 103 psi
Thermal Properties
Latent Heat of Fusion
210 J/g
Maximum Temperature: Mechanical
200 °C 400 °F
Melting Completion (Liquidus)
1090 °C 1990 °F
Melting Onset (Solidus)
1080 °C 1980 °F
Specific Heat Capacity
390 J/kg-K 0.093 BTU/lb-°F
Thermal Conductivity
260 W/m-K 150 BTU/h-ft-°F
Thermal Expansion
17 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
68 % IACS
Electrical Conductivity: Equal Weight (Specific)
69 % IACS
Otherwise Unclassified Properties
Base Metal Price
30 % relative
Density
8.9 g/cm3 560 lb/ft3
Embodied Carbon
2.6 kg CO2/kg material
Embodied Energy
40 MJ/kg 17 x 103 BTU/lb
Embodied Water
300 L/kg 36 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
51 MJ/m3
Resilience: Unit (Modulus of Resilience)
410 kJ/m3
Stiffness to Weight: Axial
7.3 points
Stiffness to Weight: Bending
18 points
Strength to Weight: Axial
12 points
Strength to Weight: Bending
14 points
Thermal Diffusivity
75 mm2/s
Thermal Shock Resistance
14 points
Alloy Composition
| Cu | 96.8 to 97.8 | |
| Fe | 2.1 to 2.6 | |
| Zn | 0.050 to 0.2 | |
| P | 0.015 to 0.15 | |
| Pb | 0 to 0.030 | |
| res. | 0 to 0.2 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM B465: Standard Specification for Copper-Iron Alloy Plate, Sheet, Strip, and Rolled Bar
Copper: Its Trade, Manufacture, Use, and Environmental Status, Gunter Joseph, 2001
ASM Specialty Handbook: Copper and Copper Alloys, J. R. Davis (editor), 2001