Half-Hard (H02) C26800 Brass
H02 C26800 brass is C26800 brass in the H02 (half hard) temper. It has the second highest ductility compared to the other variants of C26800 brass. The graph bars on the material properties cards below compare H02 C26800 brass to: wrought brasses (top), all copper alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
110 GPa 15 x 106 psi
Elongation at Break
23 %
Poisson's Ratio
0.31
Rockwell B Hardness
68
Shear Modulus
40 GPa 5.9 x 106 psi
Shear Strength
280 MPa 40 x 103 psi
Tensile Strength: Ultimate (UTS)
420 MPa 61 x 103 psi
Tensile Strength: Yield (Proof)
350 MPa 50 x 103 psi
Thermal Properties
Latent Heat of Fusion
180 J/g
Maximum Temperature: Mechanical
130 °C 270 °F
Melting Completion (Liquidus)
930 °C 1710 °F
Melting Onset (Solidus)
900 °C 1660 °F
Specific Heat Capacity
390 J/kg-K 0.092 BTU/lb-°F
Thermal Conductivity
120 W/m-K 67 BTU/h-ft-°F
Thermal Expansion
20 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
27 % IACS
Electrical Conductivity: Equal Weight (Specific)
30 % IACS
Otherwise Unclassified Properties
Base Metal Price
24 % relative
Calomel Potential
-360 mV
Density
8.1 g/cm3 510 lb/ft3
Embodied Carbon
2.7 kg CO2/kg material
Embodied Energy
45 MJ/kg 19 x 103 BTU/lb
Embodied Water
320 L/kg 38 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
90 MJ/m3
Resilience: Unit (Modulus of Resilience)
560 kJ/m3
Stiffness to Weight: Axial
7.2 points
Stiffness to Weight: Bending
19 points
Strength to Weight: Axial
14 points
Strength to Weight: Bending
15 points
Thermal Diffusivity
37 mm2/s
Thermal Shock Resistance
14 points
Alloy Composition
| Cu | 64 to 68.5 | |
| Zn | 31 to 36 | |
| Pb | 0 to 0.15 | |
| Fe | 0 to 0.050 | |
| res. | 0 to 0.3 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM B36: Standard Specification for Brass Plate, Sheet, Strip, And Rolled Bar
Copper: Its Trade, Manufacture, Use, and Environmental Status, Gunter Joseph, 2001
Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993