Half-Hard (H02) C42500 Brass
H02 C42500 brass is C42500 brass in the H02 (half hard) temper. The graph bars on the material properties cards below compare H02 C42500 brass to: wrought brasses (top), all copper alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
110 GPa 16 x 106 psi
Elongation at Break
20 %
Poisson's Ratio
0.33
Rockwell B Hardness
75
Rockwell Superficial 30T Hardness
68
Shear Modulus
42 GPa 6.1 x 106 psi
Shear Strength
270 MPa 39 x 103 psi
Tensile Strength: Ultimate (UTS)
430 MPa 63 x 103 psi
Tensile Strength: Yield (Proof)
390 MPa 57 x 103 psi
Thermal Properties
Latent Heat of Fusion
200 J/g
Maximum Temperature: Mechanical
180 °C 350 °F
Melting Completion (Liquidus)
1030 °C 1890 °F
Melting Onset (Solidus)
1010 °C 1850 °F
Specific Heat Capacity
380 J/kg-K 0.091 BTU/lb-°F
Thermal Conductivity
120 W/m-K 69 BTU/h-ft-°F
Thermal Expansion
18 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
28 % IACS
Electrical Conductivity: Equal Weight (Specific)
29 % IACS
Otherwise Unclassified Properties
Base Metal Price
30 % relative
Density
8.7 g/cm3 540 lb/ft3
Embodied Carbon
2.8 kg CO2/kg material
Embodied Energy
46 MJ/kg 20 x 103 BTU/lb
Embodied Water
330 L/kg 39 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
84 MJ/m3
Resilience: Unit (Modulus of Resilience)
680 kJ/m3
Stiffness to Weight: Axial
7.1 points
Stiffness to Weight: Bending
18 points
Strength to Weight: Axial
14 points
Strength to Weight: Bending
15 points
Thermal Diffusivity
36 mm2/s
Thermal Shock Resistance
15 points
Alloy Composition
| Cu | 87 to 90 | |
| Zn | 6.1 to 11.5 | |
| Sn | 1.5 to 3.0 | |
| P | 0 to 0.35 | |
| Fe | 0 to 0.050 | |
| Pb | 0 to 0.050 | |
| res. | 0 to 0.5 |
All values are % weight. Ranges represent what is permitted under applicable standards.