Hardened (+H) 1.7218 Steel
EN 1.7218 +H steel is EN 1.7218 steel in the hardened (H) condition. It has the highest strength compared to the other variants of EN 1.7218 steel. The graph bars on the material properties cards below compare EN 1.7218 +H steel to: EN wrought alloy steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
190 GPa 27 x 106 psi
Poisson's Ratio
0.29
Rockwell C Hardness
48
Shear Modulus
73 GPa 11 x 106 psi
Tensile Strength: Ultimate (UTS)
1550 MPa 230 x 103 psi
Thermal Properties
Latent Heat of Fusion
250 J/g
Maximum Temperature: Mechanical
420 °C 800 °F
Melting Completion (Liquidus)
1460 °C 2660 °F
Melting Onset (Solidus)
1420 °C 2590 °F
Specific Heat Capacity
470 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
44 W/m-K 26 BTU/h-ft-°F
Thermal Expansion
13 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
7.4 % IACS
Electrical Conductivity: Equal Weight (Specific)
8.5 % IACS
Otherwise Unclassified Properties
Base Metal Price
2.6 % relative
Density
7.8 g/cm3 490 lb/ft3
Embodied Carbon
1.5 kg CO2/kg material
Embodied Energy
20 MJ/kg 8.6 x 103 BTU/lb
Embodied Water
52 L/kg 6.2 gal/lb
Common Calculations
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
55 points
Strength to Weight: Bending
38 points
Thermal Diffusivity
12 mm2/s
Thermal Shock Resistance
46 points
Alloy Composition
| Fe | 96.2 to 98.1 | |
| Cr | 0.9 to 1.2 | |
| Mn | 0.6 to 0.9 | |
| C | 0.22 to 0.29 | |
| Mo | 0.15 to 0.3 | |
| Si | 0 to 0.4 | |
| Ni | 0 to 0.3 | |
| Cu | 0 to 0.3 | |
| Al | 0 to 0.040 | |
| P | 0 to 0.035 | |
| S | 0 to 0.035 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
EN 10216-2: Seamless steel tubes for pressure purposes - Technical delivery conditions - Part 2: Non-alloy and alloy steel tubes with specified elevated temperature properties
EN 10250-3: Open die steel forgings for general engineering purposes - Part 3: Alloy special steels
EN 10269: Steels and nickel alloys for fasteners with specified elevated and/or low temperature properties
EN 10263-4: Steel rod, bars and wire for cold heading and cold extrusion - Part 4: Technical delivery conditions for steels for quenching and tempering
Creep-Resistant Steels, Fujio Abe et al. (editors), 2008
Pressure Vessels: External Pressure Technology, 2nd ed., Carl T. F. Ross, 2011
Manufacture and Uses of Alloy Steels, Henry D. Hibbard, 2005
Ferrous Materials: Steel and Cast Iron, Hans Berns and Werner Theisen, 2008