Hardened H43 Tool Steel
Hardened SAE-AISI H43 is SAE-AISI H43 steel in the hardened (H) condition. The graph bars on the material properties cards below compare hardened SAE-AISI H43 to: tool steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
200 GPa 29 x 106 psi
Poisson's Ratio
0.29
Rockwell C Hardness
66
Shear Modulus
77 GPa 11 x 106 psi
Tensile Strength: Ultimate (UTS)
2140 MPa 310 x 103 psi
Thermal Properties
Latent Heat of Fusion
270 J/g
Melting Completion (Liquidus)
1530 °C 2780 °F
Melting Onset (Solidus)
1480 °C 2700 °F
Specific Heat Capacity
460 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
30 W/m-K 17 BTU/h-ft-°F
Thermal Expansion
12 µm/m-K
Otherwise Unclassified Properties
Base Metal Price
14 % relative
Density
7.9 g/cm3 500 lb/ft3
Embodied Carbon
8.2 kg CO2/kg material
Embodied Energy
120 MJ/kg 52 x 103 BTU/lb
Embodied Water
100 L/kg 12 gal/lb
Common Calculations
PREN (Pitting Resistance)
31
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
75 points
Strength to Weight: Bending
46 points
Thermal Diffusivity
8.3 mm2/s
Thermal Shock Resistance
62 points
Alloy Composition
| Fe | 83.2 to 85.9 | |
| Mo | 7.8 to 8.5 | |
| Cr | 3.8 to 4.5 | |
| V | 1.8 to 2.2 | |
| C | 0.5 to 0.65 | |
| Si | 0.2 to 0.45 | |
| Mn | 0.15 to 0.4 | |
| P | 0 to 0.030 | |
| S | 0 to 0.030 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM A681: Standard Specification for Tool Steels Alloy
Tool Steels: Properties and Performance, Rafael A. Mesquita (editor), 2016
ASM Specialty Handbook: Carbon and Alloy Steels, J. R. Davis (editor), 1996