High Shearability (+S) 1.7117 Steel
EN 1.7117 +S steel is EN 1.7117 steel in the shearability treated condition. The graph bars on the material properties cards below compare EN 1.7117 +S steel to: EN wrought alloy steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
240
Elastic (Young's, Tensile) Modulus
190 GPa 27 x 106 psi
Poisson's Ratio
0.29
Shear Modulus
72 GPa 10 x 106 psi
Tensile Strength: Ultimate (UTS)
800 MPa 120 x 103 psi
Thermal Properties
Latent Heat of Fusion
270 J/g
Maximum Temperature: Mechanical
420 °C 790 °F
Melting Completion (Liquidus)
1440 °C 2620 °F
Melting Onset (Solidus)
1400 °C 2550 °F
Specific Heat Capacity
480 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
43 W/m-K 25 BTU/h-ft-°F
Thermal Expansion
13 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
7.5 % IACS
Electrical Conductivity: Equal Weight (Specific)
8.7 % IACS
Otherwise Unclassified Properties
Base Metal Price
2.6 % relative
Density
7.7 g/cm3 480 lb/ft3
Embodied Carbon
1.5 kg CO2/kg material
Embodied Energy
21 MJ/kg 8.8 x 103 BTU/lb
Embodied Water
51 L/kg 6.0 gal/lb
Common Calculations
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
25 points
Strength to Weight: Axial
29 points
Strength to Weight: Bending
25 points
Thermal Diffusivity
12 mm2/s
Thermal Shock Resistance
24 points
Alloy Composition
| Fe | 95.2 to 96.4 | |
| Si | 1.2 to 1.5 | |
| Mn | 0.7 to 1.0 | |
| Cr | 0.7 to 1.0 | |
| Ni | 0.5 to 0.7 | |
| C | 0.49 to 0.56 | |
| P | 0 to 0.025 | |
| S | 0 to 0.025 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
EN 10089: Hot rolled steels for quenched and tempered springs - Technical delivery conditions
Manufacture and Uses of Alloy Steels, Henry D. Hibbard, 2005
Ferrous Materials: Steel and Cast Iron, Hans Berns and Werner Theisen, 2008
Steels: Processing, Structure, and Performance, 2nd ed., George Krauss, 2015