Light Annealed (O50) C19200 Copper
O50 C19200 copper is C19200 copper in the O50 (light annealed) temper. It has the second lowest strength compared to the other variants of C19200 copper. The graph bars on the material properties cards below compare O50 C19200 copper to: wrought coppers (top), all copper alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
120 GPa 17 x 106 psi
Elongation at Break
30 %
Poisson's Ratio
0.34
Shear Modulus
44 GPa 6.3 x 106 psi
Shear Strength
190 MPa 28 x 103 psi
Tensile Strength: Ultimate (UTS)
290 MPa 42 x 103 psi
Tensile Strength: Yield (Proof)
160 MPa 23 x 103 psi
Thermal Properties
Latent Heat of Fusion
210 J/g
Maximum Temperature: Mechanical
200 °C 390 °F
Melting Completion (Liquidus)
1080 °C 1980 °F
Melting Onset (Solidus)
1080 °C 1970 °F
Specific Heat Capacity
390 J/kg-K 0.092 BTU/lb-°F
Thermal Conductivity
240 W/m-K 140 BTU/h-ft-°F
Thermal Expansion
17 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
74 % IACS
Electrical Conductivity: Equal Weight (Specific)
75 % IACS
Otherwise Unclassified Properties
Base Metal Price
30 % relative
Density
8.9 g/cm3 560 lb/ft3
Embodied Carbon
2.6 kg CO2/kg material
Embodied Energy
41 MJ/kg 18 x 103 BTU/lb
Embodied Water
310 L/kg 37 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
74 MJ/m3
Resilience: Unit (Modulus of Resilience)
110 kJ/m3
Stiffness to Weight: Axial
7.2 points
Stiffness to Weight: Bending
18 points
Strength to Weight: Axial
9.0 points
Strength to Weight: Bending
11 points
Thermal Diffusivity
69 mm2/s
Thermal Shock Resistance
10 points
Alloy Composition
| Cu | 98.5 to 99.19 | |
| Fe | 0.8 to 1.2 | |
| Zn | 0 to 0.2 | |
| P | 0.010 to 0.040 | |
| Pb | 0 to 0.030 | |
| res. | 0 to 0.2 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM B465: Standard Specification for Copper-Iron Alloy Plate, Sheet, Strip, and Rolled Bar