Normalized and Tempered (+NT) 1.7383 Steel
EN 1.7383 +NT steel is EN 1.7383 steel in the normalized and tempered condition. The graph bars on the material properties cards below compare EN 1.7383 +NT steel to: EN wrought alloy steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
170
Elastic (Young's, Tensile) Modulus
190 GPa 28 x 106 psi
Elongation at Break
23 %
Fatigue Strength
210 MPa 31 x 103 psi
Impact Strength: V-Notched Charpy
38 J 28 ft-lb
Poisson's Ratio
0.29
Shear Modulus
74 GPa 11 x 106 psi
Shear Strength
350 MPa 51 x 103 psi
Tensile Strength: Ultimate (UTS)
560 MPa 81 x 103 psi
Tensile Strength: Yield (Proof)
300 MPa 44 x 103 psi
Thermal Properties
Latent Heat of Fusion
260 J/g
Maximum Temperature: Mechanical
460 °C 860 °F
Melting Completion (Liquidus)
1470 °C 2670 °F
Melting Onset (Solidus)
1430 °C 2600 °F
Specific Heat Capacity
470 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
39 W/m-K 23 BTU/h-ft-°F
Thermal Expansion
13 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
7.7 % IACS
Electrical Conductivity: Equal Weight (Specific)
8.8 % IACS
Otherwise Unclassified Properties
Base Metal Price
3.9 % relative
Density
7.9 g/cm3 490 lb/ft3
Embodied Carbon
1.8 kg CO2/kg material
Embodied Energy
23 MJ/kg 10 x 103 BTU/lb
Embodied Water
59 L/kg 7.1 gal/lb
Common Calculations
PREN (Pitting Resistance)
5.6
Resilience: Ultimate (Unit Rupture Work)
110 MJ/m3
Resilience: Unit (Modulus of Resilience)
240 kJ/m3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
20 points
Strength to Weight: Bending
19 points
Thermal Diffusivity
11 mm2/s
Thermal Shock Resistance
16 points
Alloy Composition
| Fe | 94.3 to 96.6 | |
| Cr | 2.0 to 2.5 | |
| Mo | 0.9 to 1.1 | |
| Mn | 0.4 to 0.8 | |
| Si | 0 to 0.5 | |
| Ni | 0 to 0.3 | |
| Cu | 0 to 0.3 | |
| C | 0.080 to 0.15 | |
| Al | 0 to 0.040 | |
| P | 0 to 0.025 | |
| S | 0 to 0.010 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
EN 10222-2: Steel forgings for pressure purposes - Part 2: Ferritic and martensitic steels with specified elevated temperature properties
EN 10216-2: Seamless steel tubes for pressure purposes - Technical delivery conditions - Part 2: Non-alloy and alloy steel tubes with specified elevated temperature properties
Creep-Resistant Steels, Fujio Abe et al. (editors), 2008
Microstructure of Steels and Cast Irons, Madeleine Durand-Charre, 2004
ASM Specialty Handbook: Carbon and Alloy Steels, J. R. Davis (editor), 1996
Manufacture and Uses of Alloy Steels, Henry D. Hibbard, 2005
Ferrous Materials: Steel and Cast Iron, Hans Berns and Werner Theisen, 2008
Steels: Processing, Structure, and Performance, 2nd ed., George Krauss, 2015