Quarter-Hard 304LN Stainless Steel
Quarter-hard AISI 304LN is AISI 304LN stainless steel in the quarter-hard temper. It has the second highest strength and second lowest ductility compared to the other variants of AISI 304LN stainless steel.
The graph bars on the material properties cards below compare quarter-hard AISI 304LN to: wrought austenitic stainless steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
300
Elastic (Young's, Tensile) Modulus
200 GPa 29 x 106 psi
Elongation at Break
14 %
Fatigue Strength
330 MPa 48 x 103 psi
Poisson's Ratio
0.28
Shear Modulus
77 GPa 11 x 106 psi
Shear Strength
590 MPa 86 x 103 psi
Tensile Strength: Ultimate (UTS)
980 MPa 140 x 103 psi
Tensile Strength: Yield (Proof)
580 MPa 84 x 103 psi
Thermal Properties
Latent Heat of Fusion
290 J/g
Maximum Temperature: Corrosion
420 °C 790 °F
Maximum Temperature: Mechanical
960 °C 1760 °F
Melting Completion (Liquidus)
1420 °C 2600 °F
Melting Onset (Solidus)
1380 °C 2520 °F
Specific Heat Capacity
480 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
15 W/m-K 8.7 BTU/h-ft-°F
Thermal Expansion
16 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
2.4 % IACS
Electrical Conductivity: Equal Weight (Specific)
2.7 % IACS
Otherwise Unclassified Properties
Base Metal Price
16 % relative
Density
7.8 g/cm3 490 lb/ft3
Embodied Carbon
3.1 kg CO2/kg material
Embodied Energy
44 MJ/kg 19 x 103 BTU/lb
Embodied Water
150 L/kg 18 gal/lb
Common Calculations
PREN (Pitting Resistance)
21
Resilience: Ultimate (Unit Rupture Work)
120 MJ/m3
Resilience: Unit (Modulus of Resilience)
840 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
25 points
Strength to Weight: Axial
35 points
Strength to Weight: Bending
28 points
Thermal Diffusivity
4.0 mm2/s
Thermal Shock Resistance
22 points
Alloy Composition
| Fe | 65 to 73.9 | |
| Cr | 18 to 20 | |
| Ni | 8.0 to 12 | |
| Mn | 0 to 2.0 | |
| Si | 0 to 0.75 | |
| N | 0.1 to 0.16 | |
| P | 0 to 0.045 | |
| C | 0 to 0.030 | |
| S | 0 to 0.030 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM A666: Standard Specification for Annealed or Cold-Worked Austenitic Stainless Steel Sheet, Strip, Plate, and Flat Bar
Machining of Stainless Steels and Super Alloys: Traditional and Nontraditional Techniques, Helmi A. Youssef, 2016
ASTM A182: Standard Specification for Forged or Rolled Alloy and Stainless Steel Pipe Flanges, Forged Fittings, and Valves and Parts for High-Temperature Service
ASTM A276: Standard Specification for Stainless Steel Bars and Shapes
Welding Metallurgy of Stainless Steels, Erich Folkhard et al., 2012
ASTM A959: Standard Guide for Specifying Harmonized Standard Grade Compositions for Wrought Stainless Steels
Corrosion of Austenitic Stainless Steels: Mechanism, Mitigation and Monitoring, H. S. Khatak and B. Raj (editors), 2002
Pressure Vessels: External Pressure Technology, 2nd ed., Carl T. F. Ross, 2011
Austenitic Stainless Steels: Microstructure and Mechanical Properties, P. Marshall, 1984
ASM Specialty Handbook: Stainless Steels, J. R. Davis (editor), 1994