Quarter-Hard 316 Stainless Steel
Quarter-hard AISI 316 is AISI 316 stainless steel in the quarter-hard temper. It has the second highest strength and second lowest ductility compared to the other variants of AISI 316 stainless steel.
The graph bars on the material properties cards below compare quarter-hard AISI 316 to: wrought austenitic stainless steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
290
Elastic (Young's, Tensile) Modulus
200 GPa 29 x 106 psi
Elongation at Break
11 %
Fatigue Strength
320 MPa 46 x 103 psi
Poisson's Ratio
0.28
Reduction in Area
80 %
Rockwell B Hardness
80
Shear Modulus
78 GPa 11 x 106 psi
Shear Strength
580 MPa 84 x 103 psi
Tensile Strength: Ultimate (UTS)
960 MPa 140 x 103 psi
Tensile Strength: Yield (Proof)
590 MPa 85 x 103 psi
Thermal Properties
Latent Heat of Fusion
290 J/g
Maximum Temperature: Corrosion
410 °C 770 °F
Maximum Temperature: Mechanical
590 °C 1090 °F
Melting Completion (Liquidus)
1400 °C 2550 °F
Melting Onset (Solidus)
1380 °C 2510 °F
Specific Heat Capacity
470 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
15 W/m-K 8.9 BTU/h-ft-°F
Thermal Expansion
16 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
2.3 % IACS
Electrical Conductivity: Equal Weight (Specific)
2.6 % IACS
Otherwise Unclassified Properties
Base Metal Price
19 % relative
Calomel Potential
-50 mV
Density
7.9 g/cm3 490 lb/ft3
Embodied Carbon
3.9 kg CO2/kg material
Embodied Energy
53 MJ/kg 23 x 103 BTU/lb
Embodied Water
150 L/kg 18 gal/lb
Common Calculations
PREN (Pitting Resistance)
26
Resilience: Ultimate (Unit Rupture Work)
94 MJ/m3
Resilience: Unit (Modulus of Resilience)
860 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
25 points
Strength to Weight: Axial
34 points
Strength to Weight: Bending
27 points
Thermal Diffusivity
4.1 mm2/s
Thermal Shock Resistance
21 points
Alloy Composition
| Fe | 62 to 72 | |
| Cr | 16 to 18 | |
| Ni | 10 to 14 | |
| Mo | 2.0 to 3.0 | |
| Mn | 0 to 2.0 | |
| Si | 0 to 0.75 | |
| N | 0 to 0.1 | |
| C | 0 to 0.080 | |
| P | 0 to 0.045 | |
| S | 0 to 0.030 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM A666: Standard Specification for Annealed or Cold-Worked Austenitic Stainless Steel Sheet, Strip, Plate, and Flat Bar
ASTM A182: Standard Specification for Forged or Rolled Alloy and Stainless Steel Pipe Flanges, Forged Fittings, and Valves and Parts for High-Temperature Service
ASTM A276: Standard Specification for Stainless Steel Bars and Shapes
Creep-Resistant Steels, Fujio Abe et al. (editors), 2008
Welding Metallurgy of Stainless Steels, Erich Folkhard et al., 2012
ASTM A959: Standard Guide for Specifying Harmonized Standard Grade Compositions for Wrought Stainless Steels
Corrosion of Austenitic Stainless Steels: Mechanism, Mitigation and Monitoring, H. S. Khatak and B. Raj (editors), 2002
Pressure Vessels: External Pressure Technology, 2nd ed., Carl T. F. Ross, 2011
Austenitic Stainless Steels: Microstructure and Mechanical Properties, P. Marshall, 1984
Properties and Selection: Irons, Steels and High Performance Alloys, ASM Handbook vol. 1, ASM International, 1993