Quarter-Hard (H01) C24000 Brass
H01 C24000 brass is C24000 brass in the H01 (quarter hard) temper. The graph bars on the material properties cards below compare H01 C24000 brass to: wrought brasses (top), all copper alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
110 GPa 16 x 106 psi
Poisson's Ratio
0.32
Rockwell B Hardness
52
Rockwell Superficial 30T Hardness
51
Shear Modulus
42 GPa 6.0 x 106 psi
Tensile Strength: Ultimate (UTS)
370 MPa 53 x 103 psi
Thermal Properties
Latent Heat of Fusion
190 J/g
Maximum Temperature: Mechanical
160 °C 320 °F
Melting Completion (Liquidus)
1000 °C 1830 °F
Melting Onset (Solidus)
970 °C 1770 °F
Solidification (Pattern Maker's) Shrinkage
5.5 %
Specific Heat Capacity
390 J/kg-K 0.092 BTU/lb-°F
Thermal Conductivity
140 W/m-K 81 BTU/h-ft-°F
Thermal Expansion
19 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
32 % IACS
Electrical Conductivity: Equal Weight (Specific)
34 % IACS
Otherwise Unclassified Properties
Base Metal Price
27 % relative
Density
8.5 g/cm3 530 lb/ft3
Embodied Carbon
2.6 kg CO2/kg material
Embodied Energy
43 MJ/kg 19 x 103 BTU/lb
Embodied Water
320 L/kg 38 gal/lb
Common Calculations
Stiffness to Weight: Axial
7.2 points
Stiffness to Weight: Bending
19 points
Strength to Weight: Axial
12 points
Strength to Weight: Bending
13 points
Thermal Diffusivity
43 mm2/s
Thermal Shock Resistance
12 points
Alloy Composition
| Cu | 78.5 to 81.5 | |
| Zn | 18.2 to 21.5 | |
| Fe | 0 to 0.050 | |
| Pb | 0 to 0.050 | |
| res. | 0 to 0.2 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM B134: Standard Specification for Brass Wire
ASTM B36: Standard Specification for Brass Plate, Sheet, Strip, And Rolled Bar
Copper: Its Trade, Manufacture, Use, and Environmental Status, Gunter Joseph, 2001
Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993